2015
Dimitri V. Val Mark G. Stewart

Chloride-induced corrosion of carbon steel reinforcement is the main cause of deterioration of reinforced concrete (RC) structures in marine environments. One of the ways to protect RC structures from corrosion is to use corrosion-resistant stainless steel reinforcing bars. However, stainless steel is between six and nine times more expensive than carbon steel. Thus, its use can only be justifi...

Banafsheh Norouzi Jabber Yousefi Rahime Hajinasiri Shahram Zabihi

The aim of this study was to investigate the effect of inhibition of Marrubium astranicumleaves extract on the corrosion of carbon steel in hydrochloric acid solution by using weightloss and tafel polarization methods. Inhibition was found to increase with increasingconcentration of the leaves extract. The inhibition efficiency of this extract at an optimumconcentration of 100 mg L-1 was 99.9 %...

2014
G. S. DAS

The present study is aimed to conduct the experiments in various corrosive environments at various temperatures and constant partial pressures of carbon dioxide (CO2) under dynamic condition to understand the basic mechanism and corrosion resistance of carbon steel. Usually, API grade steels are used in the pipeline for carrying the crude oil and gas. Corrosion problems constitute the major ope...

2008
B. O. Oni

The corrosion behavior of both tin-plated carbon steel and aluminum (Al 1100) in NaCl solutions were studied using electrochemical impedance spectroscopy (EIS). The study objectives were to compare their corrosion behavior in concentrated brine solution, establish the equivalent electrical circuit diagrams of their corrosion phenomena, and consequently develop steady-state corrosion models for ...

2009
Chong Li CHONG LI Srdjan Nesic Dennis Irwin

LI, CHONG, Ph.D., June 2009, Chemical Engineering Effect of Corrosion Inhibitor on Water Wetting and Carbon Dioxide Corrosion In Oil-Water Two-Phase Flow (198 pp.) Director of Dissertation: Srdjan Nesic The internal corrosion of flowlines and pipelines made from carbon steel is encountered in the oil and gas industry. The corrosion process is primarily associated with the presence of free water...

2003
Shihuai Wang Srdjan Nesic

The carbon dioxide corrosion electrochemistry of mild steel has been studied in the presence of high CO2 partial pressures and acetic acid (HAc). Potentiodynamic sweeps, linear polarization resistance (LPR) and weight loss (WL) experiments have been conducted to investigate the effects of flow velocity, CO2 partial pressure, and acetic acid concentration on the corrosion rate of mild steel. Ele...

2017
Mohita Sharma Dongshan An Tao Liu Tijan Pinnock Frank Cheng Gerrit Voordouw

Coiled tubing corrosion was investigated for 16 field water samples (S5 to S20) from a Canadian shale gas field. Weight loss corrosion rates of carbon steel beads incubated with these field water samples averaged 0.2 mm/yr, but injection water sample S19 had 1.25±0.07 mm/yr. S19 had a most probable number of zero acid-producing bacteria and incubation of S19 with carbon steel beads or coupons d...

2014
María del Carmen Camacho Oscar Galao Francisco Javier Baeza Emilio Zornoza Pedro Garcés

In the present paper, changes in mechanical properties of Portland cement-based mortars due to the addition of carbon nanotubes (CNT) and corrosion of embedded steel rebars in CNT cement pastes are reported. Bending strength, compression strength, porosity and density of mortars were determined and related to the CNT dosages. CNT cement paste specimens were exposed to carbonation and chloride a...

2015
Eman Alzahrani

The present work is aimed at examining carbon steel oil pipelines corrosion using three natural extracts (Eruca Sativa, Rosell and Mango peels) that are used as inhibitors of different concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds are used as corrosion mediums. Weight loss method was used for measuring the corrosion rate of the carbon steel specimens immersed in technical whi...

2005

In Sweden, high level radioactive waste will be disposed of in a canister with a copper outer and a cast iron or carbon steel inner. If the iron insert comes into contact with anoxic geological water, anaerobic corrosion leading to the generation of hydrogen will occur. This paper presents a study of the anaerobic corrosion of carbon steel and cast iron in artificial Swedish granitic groundwate...