The calcination reaction of two limestones and a dolomite with different porous structures was studied by thermogravimetric analysis. The effects of calcination temperature (1048-1173 K), particle size (0.4-2.0 mm), CO2 concentration (0-80 %) and total pressure (0.1-1.5 MPa) were investigated. SEM analysis indicated the existence of two different particle calcination models depending on the sor...

nanocrystalline ceria has been considered as support for carbon monoxide preferentially oxidation. in this study ceria was prepared by precipitation method and the effects of preparation conditions, such as ph of solution (8-10), aging time (1-12 hr), drying temperature (80-120 °c), calcination time (2-6 hr) and temperature (400-600 °c) were investigated on ceria synthesized powders properties....

Thermal behavior of the Shahreza dolomite ore is investigated in this paper. The hydration of the calcined dolomite was studied as a function of the calcination temperature. The DTA results exhibit three endothermic peaks at 800, 900 and 1050 °C, corresponding to decomposition of MgCO3 and CaCO3, both are present in dolomite and free calcite, respectively. The results also indicated that the de...

Considering the increasing demand for titania nanoparticles with controlled quality for various applications, the present work reports the up-scalable synthesis of size-controlled titanium dioxide nanocrystals with a simple and convenient thermal treatment route. Titanium dioxide nanocrystals with tetragonal structure were synthesized directly from an aqueous solution containing titanium (IV) i...

nanostructured alumina thin films were coated on stainless steel by sol-gel dip coating method. in order to prevent crack formation, al2o3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. effects of calcination temperature and withdrawal speed on structural properties were analyzed using xrd and sem. topography and thickness of coatings were analyzed by ...

Two nanocrystalline palladium-supported tin oxide catalysts for water denitration were synthesized by a modified sol–gel technique using appropriate chloride precursors for both support and active phases, and citric acid to tune the rate of hydrolysis and condensation. The difference among sample preparation procedures refers to the moment of the noble metal loading to the support, as well as t...

A simple and low cost detection of l-cysteine is essential in the fields of biosensors and medical diagnosis. In this study, we have developed a simple electrospinning, followed by calcination process to prepare FeCo nanoparticles embedded in carbon nanofibers (FeCo-CNFs) as an efficient peroxidase-like mimic for the detection of l-cysteine. FeCo nanoparticles are uniformly dispersed within CNF...

A bench work study was carried out to investigate the use of kaolinitic clay containing 29.4% Al2O3 extremely abundant in Saudi Arabia for the production of pure alumina by calcination at 700 o C for 1h (recommended by previous investigators) then leached by hydrochloric acid. The effects of leaching temperature (25 o C to boiling temperature), period of activation (10-150 minutes), acid concen...

In this work, a Co-Fe-Ni catalyst was prepared and the effect of a range of operational variables such as gas hourly space velocity (GHSV), calcination temperature, calcination time and agent on its catalytic performance for green-fuels production was investigated. By application of different characterization techniques such as XRD, BET, TGA/DSC, and SEM, it was found that these parameters have...

The modified thermal treatment method via alternate oxygen and nitrogen flow was successfully employed to synthesize very narrow and pure Ag nanoparticles. The structural and optical properties of the obtained metal nanoparticles at different calcination temperatures between 400 and 800 °C were studied using various techniques. The FTIR and EDX confirmed the formation of Ag nanoparticles withou...