The present study investigates the failure mechanisms of industrial fiber materials 13 a custom designed fiber cutting performance test bench. The fracture morpholog 14 fibers are examined by scanning electron microscopy. The analysis reveals that fiber cutting can be 15 distinguished according to four distinct stages of fiber failure represented by shearing, cutting, 16 brittle fracture, and t...

A leading reason for the limited use of laminated composite materials in primary structural applications is that failure initiates in the ply oriented transverse to the direction of the applied load at a much lower strain than that which would cause the ultimate failure of the laminate. Previous studies indicate that transverse failure is manifested as either cavitation induced brittle failure ...

The production of microporous carbon foams from renewable starch microcellular foam-fiber (SMCF-Fiber) composites is described. Carbon foams are used in applications such as thermal insulation, battery electrodes, filters, fuel cells, and medical devices. SMCF-Fiber composites were created from an aquagel. The water in the aquagel was exchanged with ethanol and then dried and carbonized. Higher...

As a cementitious material, geopolymers show a high quasi-brittle behavior and a relatively low fracture energy. To overcome such a weakness, incorporation of fibers to a brittle matrix is a well-known technique to enhance the flexural properties. This study comprehensively evaluates the short and long term impacts of different volume percentages of polypropylene fiber (PPF) reinforcement on fl...

We report a characterization of the acoustic sensitivity of microstructured polymer optical fiber interferometric sensors at ultrasonic frequencies from 100kHz to 10MHz. The use of wide-band ultrasonic fiber optic sensors in biomedical ultrasonic and optoacoustic applications is an open alternative to conventional piezoelectric transducers. These kind of sensors, made of biocompatible polymers,...

sudden fracture is one of the major failure modes in brittle materials. plexiglass (polymethyl methacrylate) is a well known brittle polymer, widely used in various industries. many types of notches, particularly v-shaped notches, are sometimes used in the components made of plexiglass. these notches can dramatically decrease the load bearing capacity of components due to the concentration of s...

An irregular lattice model is proposed for simulating quasistatic fracture in softening materials. Lattice elements are defined on the edges of a Delaunay tessellation of the medium. The dual sVoronoid tessellation is used to scale the elemental stiffness terms in a manner that renders the lattice elastically homogeneous. This property enables the accurate modeling of heterogeneity, as demonstr...

The fatigue behavior of the unnotched and notched silicon carbide fiber-reinforced titanium/titanium aluminide hybrid laminated composite was investigated at room temperature. The evolution of microstructural damage and its effect on stiffness and strength degradation was quantified as a function of loading cycles and applied stress levels. Fatigue crack propagation behavior and damage mechanis...

This study investigates the mechanical behavior of steel fiber-reinforced concrete (SFRC) beams internally reinforced with steel bars and externally bonded with carbon fiber-reinforced polymer (CFRP) sheets fixed by adhesive and hybrid jointing techniques. In particular, attention is paid to the load resistance and failure modes of composite beams. The steel fibers were used to avoiding the rip...

The present study investigates the failure mechanisms of industrial fiber materials, using a custom designed fiber cutting performance test bench. The fracture morphologies of single PA6 fibers are examined by scanning electron microscopy. The analysis reveals that fiber cutting can be distinguished according to four distinct stages of fiber failure represented by shearing, cutting, brittle fra...