A series of stress corrosion experiments were performed on 12 pultruded glass fiber composite materials (two fibers in six different matrices) commonly used in high voltage composite insulators. In this study two types of glass fibers were investigated, namely Eglass and ECR-glass. The tests were performed in nitric acid solutions (pH 1.2) using constant K I specimens that were specifically des...

--The inhibition of the corrosion of mild steel in hydrochloric acid solutions by the extract of Artemisia Herba-Alba has been studied using gravimetric and electrochemical measurement. Inhibition was found to increase with increasing concentration of the inhibitor. Values of inhibition efficiency calculated from weight loss and potentiodynamic polarization are in good agreement. This value goe...

Cyclic voltammetric studies were carried out on the deposition of polyaniline on pure aluminum from oxalic acid solution with and without different anions (CO3, SO3, SO4, DBS) and contribution of these anions to lyaniline film formation was investigated. Corrosion behavior of polyaniline coated aluminum in oxalic acid solution with and without different anions (CO3, SO3, SO4, DBS) has been inve...

The corrosion of bronzes was examined in the context of single-acid versus mixed-acid (as in urban acid rain) solutions. Two bi-component bronzes (copper with either 3% Sn or 7% Sn) that closely represent those of historic artifacts were immersed for five weeks in conditions designed to replicate those experienced by statues and ornaments in cities where rainfall and humidity constantly produce...

Atmospheric corrosion is a significant problem given destruction of various materials, especially metals. The corrosion investigation in the industrial city environment was carried out during one year exposure. Corrosion potential was determined using the potentiometric method. The highest effect of corrosion processes was observed during the winter season due to increased air pollution. Corros...

The corrosion behaviour of aluminium and6063 aluminium alloy was investigated in phosphoric acid of different concentrations at different temperatures. The study was done by electrochemical method, using Tafel polarization and electrochemical impedance spectroscopy (EIS) techniques. The kinetic parameters and thermodynamic parameters were calculated using Arrhenius theory and transition state t...

Abstract—Corrosion inhibitors are widely used in concrete industry to reduce the corrosion rate of steel rebar which is present in contact with aggressive environments. The present work aims to using Zamzam water from well located within the Masjid al-Haram in Mecca, Saudi Arabia 20 m (66 ft) east of the Kaaba, the holiest place in Islam as corrosion inhibitor for steel in rain water and simula...

Corrosion of 1020 carbon steel coupons in natural seawater over a 1-year period was more aggressive under strictly anaerobic stagnant conditions than under aerobic stagnant conditions as measured by weight loss and instantaneous corrosion rate (polarization resistance). Under oxygenated conditions, a two-tiered oxide layer of lepidocrocite/goethite formed. The inner layer was extremely tenaciou...

The effects of metallurgical factors on the aqueous corrosion behavior of highentropy alloys (HEAs) are reviewed in this article. Alloying (e.g., Al and Cu) and processing (e.g., heat treatments) effects on the aqueous corrosion behavior of HEAs, including passive film formation, galvanic corrosion, and pitting corrosion, are discussed in detail. Corrosion rates of HEAs are calculated using ele...