MO XF, FAN DB, QIN TF & CHU FX. 2015. Curing characteristics and adhesion performance of phenol–formaldehyde resins with composite additives. The curing characteristics of cure-accelerated phenol–formaldehyde resins with composite additives were investigated by differential scanning calorimetry analysis and gelation test. The pot lives and adhesion performances of phenol–formaldehyde resins wer...

Several techniques have been used for sand production control in sandstone reservoirs.The main objective of this research is to present a suitable resin to be used as a consolidation agent in oil reservoirs. To achieve this purpose, urea-formaldehyde resin, phenol-formaldehyde resin, and modified urea-formaldehyde resin were selected to be studied. Core samples were made by the sand sample prov...

partial replacement of formaldehyde with furfural in the urea-formaldehyde resin on the formaldehydeemission, physical and mechanical properties of particleboard was investigated. the modulus ofrupture (mor), modulus of elasticity (moe), internal bond (ib), water absorption (wa), thicknessswelling (ts) and formaldehyde emission (fe) of poplar particleboards made with the modifiedresins were mea...

Approximately 1 million metric tons of urea-formal-dehyde resin are produced annually. More than 70% of this urea-formaldehyde resin is used by the forest products in-*This information was written and prepared by a U.S. Government employee on official time and it is, therefore, in the public domain and not subject to copyright.

This study reports the results of a study aimed at reducing the free formaldehyde content of Phenolformaldehyde resin by using Urea as means for forming a reversible adduct with formaldehyde. The highly volatile formaldehyde has an unpleasant odour and irritates the eyes and nasal passages. The free formaldehyde content (FFC) of the modified resol resin was determined by titration method. With ...

Urea-formaldehyde is one of the commonly used resin types in particleboard industry. In this study, effect nanofibrillated cellulose (NFC) and titanium dioxide (TiO2) addition formulation urea formaldehyde on physical, mechanical, morphological properties samples was investigated. The NFC (0.5% 1%) TiO2 (0.5%, 1%, 2%) were added to 10% adhesive formulation. Two different pressure times, 4 8 min...

The reinforcing impact of Lignocellulosic micro and nanofibrillated cellulose (L-MNFCs) obtained from Eucalyptus Globulus bark in Urea-Formaldehyde UF adhesive was tested. L-MNFCs were prepared by an environmentally friendly, low-cost process using a combination involving steam explosion followed refining ultra-fine grinding. Obtained showed web-like morphology with some aggregates lignin nanod...

there are adequate sources for wood adhesives, but scarcity of oil resources can affect the cost and future availability of oil based resins. for avoiding of this process, seeking for feasibility of replacement of these oil feedstocks is necessary. in present work, thermal behavior of urea formaldehyde resin modified by furfural was investigated. the thermo-gravimetry was used for this purpose,...

Composites based on waste products from the production of 5-hydroxymethylfurfural - "humins" and melamine or urea (as a cross-linking agent) with wood fl our filler, 70 % by weight) were obtained. Studies physical mechanical properties materials different contents have been carried out, which shown that composites humins: (2,5: 1) humins:urea (2:1) tensile strength 150 165 MPa, respectively, si...