Sol–gel process was used for the preparation of Rhodamine 6G (R6G) doped silica xerogels, using tetraethylorthosilicate [TEOS, Si(OC2H5)4] as the precursor for the silica network. Silica alcosol was prepared by hydrolysis and polycondensation of ethanol (EtOH) diluted TEOS in the presence of citric acid (CTA) catalyst. The ethanolic R6G was added to the alcosol to trap R6G molecules inside the ...

Sol–gel films were prepared using different ratios of two silica precursors, vinyltrimethoxysilane (VTMS) and tetraethylorthosilicate (TEOS), targeting the anticorrosion treatment of aluminum alloy 2024-T3. The electrochemical behavior of the alloy coated with such films, which was studied in a 0.05 mol L -1 NaCl solution, revealed that the VTMS/TEOS ratio drastically affects the anticorrosion ...

The extensive research activity on sol-gel processing of silica glass has been reviewed by several authors [l-4]. The typical alkoxide route to silica sols comprises the catalyzed reaction of tetraethoxysilane (TEOS) and water in a mutual solvent. The TEOS alkoxy groups hydrolyze to form silanol monomers which condense and crosslink to form the silica gel network. The nature of the sol and the ...

Experimental studies of gas-phase nanoparticle coating by photoinduced chemical vapor deposition (photoCVD) have shown that silica coatings can be produced with controllable thicknesses on different nanoparticle cores for a variety of applications. This study presents a chemical reaction sequence for the photo-CVD process to describe the production of silica coatings from the decomposition of t...

A novel sol-gel hybrid methyltrimethoxysilane-tetraethoxysilane (MTMOS-TEOS) was produced and applied as sorbent for solid phase extraction (SPE). Five selected organophosphorus pesticides (OPPs) were employed as model compounds to evaluate the extraction performance of the synthesized sol-gel organic-inorganic hybrid MTMOS-TEOS. Analysis was performed using gas chromatography-mass spectrometry...

Kirja on nimensä mukaisesti yleisesitys Deweyn esteettisestä teoriasta. Samalla se esteettis-filosofinen tutkielma, joka puolustaa teorian omaperäisyyttä ja paikkaa nykytutkimuksen pohjana. Kaksinaisen tavoitteensa vuoksi kirjassa pienimuotoinen sisäinen jännite: onko yleisteos, suunnattu kaikille ajattelusta kiinnostuneille vai erityisesti juuri estetiikan tutkijoille puheenvuoro?

Hybrid sol-gel-derived xerogel films prepared from 45/55 (mol ratio) n-propyltrimethoxysilane (C3-TMOS)/tetramethylorthosilane (TMOS), 2/98 (mol ratio) bis[3-(trimethoxysilyl)propyl]-ethylenediamine (enTMOS)/tetraethylorthosilane (TEOS), 50/50 (mol ratio) n-octyltriethoxysilane (C8-TEOS)/TMOS, and 50/50 (mol ratio) 3,3,3-trifluoropropyltrimethoxysilane (TFP-TMOS)/TMOS were found to inhibit sett...

We investigate the controlled release of lidocaine hydrochloride from the doped silica-based xerogels. In the xerogel preparation, tetraethoxysilane (TEOS), methyltriethoxysilane (MTES), and propyltriethoxysilane (PTES) are used as precursors, and a nonionic surfactant Igepal CO 720 is used as a dopant. The experimental results suggest that the release of lidocaine hydrochloride can be easily c...

We report the fabrication of large area, thin asymmetric free-standing two-dimensional (2-D) photonic crystals. We fabricate large area 2-D close-packed monodisperse polystyrene (PS) particle monolayers at air/water interfaces by using our needle tip flow method. We then layer tetraethyl orthosilicate (TEOS) onto the 2-D array to form a thin TEOS layer on the 2-D particle array on water. The he...

Mixtures of n-octadecyltrimethoxysilane (C18, 1-5 mole-%), n-octyltriethoxysilane (C8) and tetraethoxysilane (TEOS) gave xerogel surfaces of varying topography. The 1:49:50 C18/C8/TEOS xerogel formed 100-400-nm-wide, 2-7-nm deep pores by AFM while coatings with ≥3% C18 were free of such features. Segregation of the coating into alkane-rich and alkane-deficient regions in the 1:49:50 C18/C8/TEOS...