A mullite/mullite nanocomposite powder has been synthesized, composed of nanometer-size 3Al2O3 · 2SiO2 (‘3 : 2’) mullite precipitates within a matrix of the high alumina 2Al2O3 · SiO2 (‘2 : 1’) mullite. Historically, the transition from the metastable high-alumina phase to the thermodynamically stable ‘3 : 2’ phase of mullite has been thought to be a continuous process, involving a continuous s...

The effect of Au addition on the microstructural and the tensile properties of Sn–0.7 mass%Cu alloy was examined. Tensile strength and 0.2% proof stress remarkably increase up to 0.3 mass%Au primarily due to solid solution hardening. Beyond 0.3 mass%Au, due to precipitation of large intermetallic compounds, elongation decreases while tensile strength and 0.2% proof stress increase slightly. Wit...

The mechanical properties of a die-cast Al–Si–Cu alloy (DC ADC12) were improved using new processing techniques that induce grain refinement and precipitation hardening. Several gravity-cast ADC12 (GC samples with different microstructural sizes also evaluated to better understand the material DC ADC12. indicate has both advantages (fine grains) disadvantages (defects). can be by adding Na befo...

We report a computational 'alloy by design' approach which can significantly accelerate the design process and substantially reduce the development costs. This approach allows simultaneously optimization of alloy composition and heat treatment parameters based on the integration of thermodynamic, thermo-kinetics and a genetic algorithm optimization route. Novel steel compositions and associated...

The relationship between microstructure and tensile properties of an Nb–Ti microalloyed X90 pipeline steel was studied as a function of finish rolling temperature using a Gleeble 3500 simulator, an optical and scanning electron microscope, electron back scattered diffraction (EBSD), a transmission electron microscope (TEM) and X-ray diffraction. The results indicate that the microstructure is p...

The effects of Si addition on the precipitation hardening behaviour and evolution of intergranular corrosion (IGC) of Al-Mg-Si alloys were investigated using hardness tests, scanning electron microscopy (SEM), potentiodynamic polarization measurements, and high-resolution transmission electron microscopy (HRTEM). With an increase of the Si content, the peak hardness of the Al-Mg-Si alloys consi...