The use of Fiber Reinforced Polymer (FRP) reinforcement is a practical alternative to conventional steel rebars in concrete structures subjected to aggressive environments. The solution is attractive for bridge deck and rail applications, as it eliminates corrosion of the steel reinforcement, which is the major instrument of degradation. Due to the peculiar physical and mechanical characteristi...

t h r o u g h SEM and SAM Measurement of the fiber orientation is one of the most important inspection items 2.1 Orientation of the Molding Cross to examine the shape and strength of the Section through SEM products[ll. The 3D fiber orientation has been measured by analyzing the elliptical marks of the cross section of the fiber from the photograph of the FRP. In these methods, i t is not possi...

* Corresponding author. Abstract – Recent improvements in sensor capabilities have enabled fire characterization from satellites. Instantaneous intensities of active fires have been characterized by the Fire Radiative Power (FRP), while burn severity has been assessed from the evaluation of Normalized Burn Ratios (NBR) derived from preand post-fire multispectral imagery. MODIS on the Terra and ...

[Purpose] The purpose of this study was to investigate the effect of the timing of leg support elevation on the horizontal force acting on the buttocks in a reclining wheelchair. [Subjects and Methods] The participants were 17 healthy men. Two experimental conditions were tested: the leg-down and leg-up conditions. The back support was reclined at increasing angles, from the initial upright pos...

Fiber reinforced polymer (FRP) composites offer very high strength-to-weight and stiffness-to-weight ratios. As a result, the aerospace industry is making a major effort to incorporate an increasing number of composite materials into various components and structures. However, machining of FRP composites is one of the most difficult and least understood areas in manufacturing technology. Thus, ...

The use of fiber reinforced polymer (FRP) bars in reinforced concrete members enhances corrosion resistance when compared to traditional steel reinforcing bars. Although there is ample research available on the behavior of FRP bars and concrete members reinforced with FRP bars under elevated temperatures (due to fire), there is little published information available on their post-fire residual ...

Fiber Reinforced Polymer (FRP) systems have gained much popularity as a method for reinforcing existing concrete structures. However a variety of sudden failure methods, such as debonding, delamination, and creep rupture have led to the development of code limitations on the strength that an FRP system can be considered to provide. The uncertainty brought on by the failure methods mentioned abo...

Failures in FRP-strengthened reinforced concrete (RC) members may occur by flexural failures of critical sections or by debonding of FRP plate from the RC beams. Debonding in the FRP/adhesive/concrete interface region may cause a significant decrease in member capacity leading to a premature failure of the system. There is a need for improved knowledge of the debonding processes under mechanica...

The current paper reviews existing design guidelines for strengthening beams in shear with carbon fibre reinforced polymer (CFRP) sheets and proposes a modification to Concrete Society Technical Report TR55. It goes on to present the results of an experimental programme which evaluated the contribution of CFRP sheets towards the shear strength of continuous reinforced concrete (RC) beams. A tot...

In aerospace and many types of civil infrastructure applications, the use of adhesive-bonded composite joints have been constantly increasing. In this study, fracture behaviour of adhesively bonded single lap joint (SLJ) with pre-existing damage at the interface of free edge of the top adherend and adhesive along the width of the joint is studied by strain energy release rate (SERR) approach us...