In this paper, rotating bending fatigue tests of 2024-T4 Al alloy with different oxide coatings were carried out. Compared to the uncoated and previously reported oxide coatings of aluminum alloys, the fatigue strength is able to be enhanced by using a novel oxide coating with sealing pore technology. These results indicate that the better the coating surface quality is, the more excellent the ...

Fatigue-crack-growth tests were conducted on compact, C(T), specimens made of D16Cz (clad) aluminum alloy under constant-amplitude loading, a single spike overload, and simulated aircraft spectrum loading. Constant-amplitude tests were conducted to generate crack-growth-rate data from threshold to near fracture over a wide range of stress ratios (R = Pmin/Pmax = 0.1–0.75) using the new compress...

The objective of this work is to provide a rationale approach to de®ne the limiting conditions for high-cycle fatigue (HCF) in the presence of foreign-object damage (FOD). This study focused on the role of simulated FOD in a€ecting the initiation and early growth of small surface fatigue cracks in a Ti±6Al±4V alloy, processed for typical turbine blade applications. Using high-velocity (200±300 ...

INTRODUCTION Stress fractures are common in athletes, military recruits, and Thoroughbred racehorses, and may occur as hip fractures in the elderly. All of these injuries, to some extent, depend upon the propagation of fatigue cracks. Therefore, it is important to characterize the rates at which fatigue cracks grow and how microstructural differences found in cortical bone influence the crack g...

Ultra High Cycle fatigue leads to a failure initiated in the bulk material of a material. Some results on the nodular cast iron are presented: initiation occurs from the defects, located at the surface or in the bulk. It has been shown that environment plays a major role that could explain the difference between fatigue lives, for the surface and internal initiation. The influence of the defect...

A numerical technique for modeling fatigue crack propagation of multiple coplanar cracks is presented. The proposed method couples the extended finite element method (X-FEM) [Int. J. Numer. Meth. Engng. 48 (11) (2000) 1549] to the fast marching method (FMM) [Level Set Methods & Fast Marching Methods: Evolving Interfaces in Computational Geometry, Fluid Mechanics, Computer Vision, and Materials ...

As cyclic fatigue is considered to be a major cause of clinical tooth fractures, achieving a comprehensive understanding of the fatigue behavior of dentin is of importance. In this note, the fatigue behavior of human dentin is examined in the context of the Kitagawa-Takahashi diagram to define the limiting conditions for fatigue failure. Specifically, this approach incorporates two limiting thr...

A model has been developed to predict crack opening and closing behavior for propagating fatigue cracks which undergo significant sliding displacements at crack flanks. Crack surfaces were described statistically by assuming a random distribution of asperity heights and a mean density of asperities and asperity radii. The propagating crack was subdivided into strips, and each strip was treated ...

Fatigue of materials, like alloys, is basically fatigue-crack growth in small cracks nucleating and growing from micro-structural features, such as inclusions voids, or at micro-machining marks, large to failure. Thus, the traditional nucleation stage (Ni) microcracks (initial flaw sizes 1 30 μm about 250 μm) metal alloys. crack-growth tests were conducted on a 9310 steel under laboratory air r...

Recent studies have shown that nanotwinned copper (NT Cu) exhibits a combination of high strength and moderate ductility. However, most engineering and structural applications would also require materials to have superior fracture toughness and prolonged subcritical fatigue crack growth life. The current study investigates the effect of twin density on the crack initiation toughness and stable ...