Axial loading tests with stress ratios R of -1, 0 and 0.3 were performed to examine the fatigue failure behavior of a carburized Cr-Ni steel in the long-life regime from 10⁴ to 10⁸ cycles. Results show that this steel represents continuously descending S-N characteristics with interior inclusion-induced failure under R = -1, whereas it shows duplex S-N characteristics with surface defect-induce...

The growth of transverse cracks under expanding spherical contact in a model system consisted of soda-lime glass bonded to a polycarbonate substrate is observed in situ from below or from the polished edge of the bilayer. Abrasion or chemical etching is employed on the coating surfaces to control the initial fracture. In the limit case of monoliths, the crack mouth becomes fully engulfed by the...

While the formation of cracks is often stochastic and considered undesirable, controlled fracture would enable rapid and low cost manufacture of micro/nanostructures. Here, we report a propagation-controlled technique to guide fracture of thin films supported on soft substrates to create crack arrays with highly controlled periodicity. Precision crack patterns are obtained by the use of strateg...

Cracks, the important factor of structure failure, reflect structural damage directly. Thus, it is significant to realize distributed, real-time crack monitoring. To overcome the shortages of traditional crack detectors, such as the inconvenience of installation, vulnerability, and low measurement range, etc., an improved topology-based cable sensor with a shallow helical groove on the outside ...

A basic assumption often made in risk/reliability based inspection planning is that a Bayesian approach can be used. This implies that probabilities of failure can be updated in a consistent way when new information (from inspections and repairs) becomes available. The Bayesian approach and a no-crack detection assumption implies that the inspection time intervals usually become longer and long...

Brittle materials such as rock and ceramic usually exhibit apparent increases of strength and toughness when subjected to dynamic loading. The reasons for this phenomenon are not yet well understood, although a number of hypotheses have been proposed. Based on dynamic fracture mechanics, the present work offers an alternate insight into the dynamic behaviors of brittle materials. Firstly, a sin...

One of the most important problems in the fatigue analysis and design of aircraft structures is the prediction of the fatigue crack growth in service. Available in-service inspection data for various types of aircraft indicate that the fatigue crack damage accumulation in service involves considerable statistical variability. In this paper, we consider the problem of estimating the minimum time...

Concern over construction vibration-induced cracking has led to development of a new approach to vibration monitoring, an autonomous crack comparometer (ACC). This paper describes sensor performance and chronicles the first steps in the development of this concept, illustrated in Figure 1. A single sensor measures both weather-induced micrometer changes in crack width and those produced by habi...

The mode II initiation fracture toughness of wood was measured by the three-point bend endnotched flexure (3ENF) test for various crack lengths, and the dependence of toughness on the crack length was analyzed by the four conventional methods of data reduction : elementary beam theory, Williams end correction method, and two compliance calibration methods. In addition to these methods, the comp...

The objective of the current study is to determine the fatigue limit of a clean and high-performance material named as HSLA-100 steel and to compare the obtained fatigue limit with that of theoretically predicted fatigue limit by statistics of extreme value (SEV) method. Also, the size of inclusions located at the site of fatigue crack nucleation on the fracture surface of the fatigue test spec...