Powder of La0.6Sr0.4CoO3-α (LSCO) was synthesized by a combined citrate-EDTA method. The as-synthesized LSCO powder was calcined, respectively at temperatures of 800, 900 and 1000 °C with different heating/cooling rates which are 2, 5, 10 and 15 °C min. The effects of heat treatments on the phase formation of perovskite phase of LSCO were investigated by powder X-ray diffraction (XRD). The XRD ...

Pressure- and temperature-induced phase transitions have been studied for more than a century but very little is known about the non-equilibrium processes by which the atoms rearrange. Shock compression generates a nearly instantaneous propagating high-pressure/temperature condition while in situ X-ray diffraction (XRD) probes the time-dependent atomic arrangement. Here we present in situ pump-...

Self-assembled organic-inorganic CH3NH3PbI3 perovskite microwires (MWs) upon humidity exposure along several weeks were investigated by photoluminescence (PL) spectroscopy, Raman spectroscopy, and X-ray diffraction (XRD). We show that, in addition to the common perovskite decomposition into PbI2 and the formation of a hydrated phase, humidity induced a gradual PL redshift at the initial weeks t...

In this paper, Zn2SiO4:xEu3+ phosphors were synthesized with different concentrations of Eu3+ ions (x = 1, 3 and 5 wt.%) by using waste bottle glasses as silicate source. The structure, morphology, and luminescent properties of the phosphors were characterized using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and photoluminescence (PL) spectroscopy. The XRD ana...

In the present research program, cost effective and environment friendly gold nanoparticless were synthesized using the onion (Allium cepa) extract as the reducing agent. The nanoparticless were characterized using UV-visble, XRD, and SEM, TEM methods. The absorption peak at 540 nm was found to be broaden with increase in time indicating the polydispersity nature of the nanoparticles. The XRD r...

The powders of Ba(Ce1-xZrx)0.90Y0.1O3-δ (BCZY) with 0.2 ≤ x ≤ 0.6 have been prepared by a modified sol-gel method. Triethylenetetramine (TETA) was employed as chelating agent. Phase formation of calcined powders at 1100C and sintered pellets at 1400C of BCZY were examined by an X-ray diffractrometer (XRD). XRD results showed the calcined powder and sintered pellet formed a single perovskite pha...

Cobalt oxide (Co3O4) nanoparticles were successfully prepared by thermal decomposition of cobalt hydroxide synthesized from cobalt acetate, ammonium hydroxide and 10% glycerol. The cobalt oxide nanoparticles calcined at 450 °C were characterized by using XRD. The XRD confirms the crystallinity and crystal structure of the sample. It also shows that the diffraction peak are broadened which revea...

In the present investigation, the oxidizing roasting process of chromite with sodium carbonate to prepare potassium dichromate crystals was studied in the microwave field with air, by heating the chromite and sodium carbonate. The chromite and sodium carbonate heated separately at 1000 ◦C in the microwave oven (frequency: 2.45 GHz; power 1.5 kW) in order to study the microwave absorption proper...

Rhombohedral Boron Nitride (r-BN) layers were grown on sapphire substrate in a hot-wall chemical vapor deposition reactor. Characterization of these layers is reported in details. Xray diffraction (XRD) is used as a routine characterization tool to investigate the crystalline quality of the films and the identification of the phases is revealed using detailed pole figure measurements. Transmiss...