This study reports the simple process to synthesis of CuO/CuI nanocomposite in a non-aqueous solution. In the conducted experiments CuI and Dimethyl Sulfoxide (DMSO) were used as the precursors. Moreover, DMSO had role of solvent and ligand simultaneously. In experiments the effects of oleic acid as the particles size modifier, temperature and concentration were investigated. Crystalline struct...

the nanoparticles of ti and tio2 have attracted extensive research interest because of their diverse applications in, for instance, catalysis, energy conversion, pigment and cosmetic manufacturing and biomedical engineering. through this project, a one-step bulk synthesis method of electromagnetic levitational gas condensation (elgc) was utilized for the synthesis of monodispersed and crystalli...

in this research controlled coating of magnetite (fe3o4) nanoparticles with sio2 was investigated. the fe3o4 nanoparticles were synthesized via chemical co-precipitation and then coated by silica according to stober method. effects of tetra ethyl ortho silicate (teos) concentration and ethanol to teos on the coating thickness were investigated. x-ray powder diffraction, fourier transform infrar...

zinc oxide (zno) nanopowders were synthesized by the sol–gel method from an ethanol solution of zinc sulfate heptahydrate in the presence of diethylene glycol surfactant. detailed structural and microstructural investigations were carried out using x-ray diffraction (xrd), high-resolution transmission electron microscopy (hrtem), field emission scanning electron microscopy (fe-sem), fourier tra...

The nanoparticles of gold doped with various percentage of copper (Cu 10%, 25%, 75%) were synthesized by wet-chemical method at room temperature. Copper (II) sulfate and gold (III) chloride trihydride was taken as the metal precursor and ascorbic acid as a reducing agent and anhydride maleic as surfactant. The reaction is performed with high-speed stirring at room temperature under nitrogen atm...

Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stag...