Fullerene (C60)-enhanced Bi2TiO4F2 hierarchical microspheres were prepared by a facile solvothermal method. Compared to the pure Bi2TiO4F2 photocatalyst, the C60/Bi2TiO4F2 samples exhibit much stronger photocatalytic performance for degrading Rhodamine B (RhB) and Eosin Y (EY) under visible light irradiation. Such greatly enhanced photocatalytic activity may be ascribed to strong combination an...

the photocatalytic activity of nano-bi2o3 was evaluated in degradation of rhodamine b (rhb) as a model of dye pollutant from waste waters. nano sized bi2o3 was synthesized using the chemical precipitation method. the as-prepared sample was characterized by x-ray diffraction (xrd), scanning electron microscopy (sem) and fourier transform infrared spectrometry (ft-ir). structural analysis reveale...

A simple and straightforward approach to prepare TiO2-coated carbon nanotubes (CNTs) is presented. Anatase TiO2 nanoparticles (NPs) with the average size ~8 nm were coated on CNTs from peroxo titanic acid (PTA) precursor even at low temperature of 100 °C. We demonstrate the effects of CNTs/TiO2 molar ratio on the adsorption capability and photocatalytic efficiency under UV-visible irradiation. ...

The photocatalytic degradation of organic compounds of olive mill wastewater (OMWW) was investigated by using core-shell-shell Fe3O4/SiO2/TiO2 nanoparticles as catalyst. The preparation of nanoparticles was performed by coating onto magnetic nanoparticles a SiO2 layer, using Stober method and TiO2 layer, using sol-gel method. The photo catalyst was characterized by dynamic light scattering (DLS...

Photocatalytic oxidation of sodium salt of 2,6-dichloroindophenol (DCIP) in titanium dioxide aqueous suspension has been studied. DCIP is photocatalytically oxidized on the active Ti02 surface by the medium pres­ sure Hg lamp with pyrex sleeve radiation (A>280nm). The apparent integral quantum yield of the DCIP decomposition was determined. Photocatalytic decomposition of DCIP in aqueous suspen...

Gd(2)InSbO(7) and Gd(2)FeSbO(7) were synthesized first, and their structural and photocatalytic properties were studied. The lattice parameters and the band gaps for Gd(2)InSbO(7) and Gd(2)FeSbO(7) were 10.449546 Å, 10.276026 Å, 2.897 eV and 2.151 eV. The photocatalytic degradation of rhodamine B was performed with Gd(2)InSbO(7) and Gd(2)FeSbO(7) under visible light irradiation. Gd(2)InSbO(7) a...

Er(3+)-TiO(2) synthesized by a surfactant free hydrothermal method exhibits good photoactivities under sun-like excitation for the degradation of phenol. The presence of Er(3+) does not affect the structural and morphological features of the TiO(2) significantly. The best photocatalytic performance was attained for the samples with 2 wt% of Er. Different photocatalytic runs indicated that the i...

A novel Cu1.8Se/Cu₃Se₂ composite photocatalyst was prepared by the simple precipitation method. This composite possesses a wide photoabsorption until the range of near-infrared light, and exhibits significantly enhanced photocatalytic activity for methyl orange degradation under visible and near-infrared light irradiation compared with bare Cu1.8Se and Cu₃Se₂. The mechanism of this outstanding ...

We demonstrate plasmonic enhancement of photocatalytic water splitting under visible illumination by integrating strongly plasmonic Au nanoparticles with strongly catalytic TiO2. Under visible illumination, we observe enhancements of up to 66× in the photocatalytic splitting of water in TiO2 with the addition of Au nanoparticles. Above the plasmon resonance, under ultraviolet radiation we obser...