Fatigue crack growth rate depends not only on the load amplitude, but also on the morphology of crack path. The strain energy density theory has the ability to analyze crack growth rate. A strain energy density crack growth model is proposed. It can predict the lifetime of fatigue crack growth for mixed mode cracks while an equation for mode I crack is also obtained. The validity of the model i...

structural health monitoring of cracked structures is one of beloved subject of researchers recently. consider of crack behavior in the water and energy pipeline is important because of environmental problems. in this paper consider of crack parameters in the underwater pipe subjected to mechanical transient load is investigated. for this purpose, three- dimensional parametric model of cracked ...

Turbo generator shafts are often subjected to cyclic torsion resulting in formation of large longitudinal cracks as well as circumferential cracks. The presence of these cracks could greatly impact the shaft resonance frequencies. In this paper, dynamic response of a shaft with longitudinal and circumferential cracks is investigated through a comprehensive analytical study. The longitudinally c...

Fatigue cracking is one of the most common failure modes of various load-bearing structures. Even though sensors of many different types have been developed for crack detection, very few can monitor crack growth with a high sensitivity. This paper presents an antenna sensor that is capable of monitoring the growth of fatigue cracks with a sub-millimeter resolution. According to microstrip patch...

Fatigue crack growth behavior of AZ61 magnesium alloy was investigated in low humidity (55% relative humidity) and 3.5% NaCl spray environments under various stress ratios. Fatigue crack growth rates became higher with increasing load ratio for both environments. However, the results of fatigue crack growth test under 3.5% NaCl spray environment showed lower fatigue crack propagation rate compa...

An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...

Crack emerged in the late 1980s in Brazil. This emergence was a critical moment for public health; the growing AIDS epidemic led intravenous cocaine users to migrate toward crack use to avoid the use of injection drugs. At the same time, young consumers of marijuana also began using crack, largely due to market strategies in drug trafficking that led to a shortage of marijuana and the availabil...

BACKGROUND In Brazil, crack cocaine use remains a healthcare challenge due to the rapid onset of its pleasurable effects, its ability to induce craving and addiction, and the fact that it is easily accessible. Delayed action on the part of the Brazilian Government in addressing the drug problem has led users to develop their own strategies for surviving the effects of crack cocaine use, particu...

A permeable crack model is proposed to analyze crack growth in a piezoelectric ceramic. In this model, a permeable crack is modeled as a vanishing thin, finite dimension, rectangular slit with dielectric medium inside. A first-order approximation solution is derived in terms of the slit height, h0 . The main contribution of this paper is that the newly proposed permeable crack model reveals tha...

The mechanisms of fatigue-crack propagation are examined with particular emphasis on the similarities and differences between cyclic crack growth in ductile materials, such as metals, and corresponding behavior in brittle materials, such as intermetallics and ceramics. This is achieved by considering the process of fatiguecrack growth as a mutual competition between intrinsic mechanisms of crac...