Ditte Caroline Andersen,1,2,* Charlotte Harken Jensen,1 and Søren Paludan Sheikh1,3 1Laboratory of Molecular and Cellular Cardiology, Department of Clinical Biochemistry and Pharmacology, Odense University Hospital, 5000 Odense C, Denmark 2Clinical Institute/University of Southern Denmark, 5000 Odense C, Denmark 3Institute of Molecular Medicine/University of Southern Denmark, 5000 Odense C, Den...

The aluminum-L,,VV Auger spectra for elemental Al. Al oxide and Al nitride have been measured in an assessment of the utility of Auger spectroscopy in characterizing thin oxidized Al films used in model supported-metal catalyst studies. Clearly distinct spectra were found for the three surface chemical states. The oxide spectrum was shown to be similar to published spectra from bulk, single-cry...

The change of microstructure of the title alloys with concentration, temperature and applied thermal treatment was studied in situ by XRD. The alloys, having the Zn atomic fraction, x(Zn), from 0.03 to 0.62, were subjected to: (i) rapid quenching from a temperature, Tt, higher than the solid-solution temperature, Tss, in water at RT (samples WQ); (ii) slow cooling from Tt to RT (samples SC). Th...

There is variability in the Mg isotopic composition that is a reflection of the widespread heterogeneity in the isotopic composition of the elements in the solar system at approximately 100 ppm. Measurements on a single calcium-aluminum-rich inclusion (CAI) gave a good correlation of Mg ⁄ Mg with Al ⁄ Mg, yielding an isochron corresponding to an initial (Al ⁄ Al)o = (5.27 ± 0.18) · 10 and an in...

Precipitation strengthening is investigated in binary Al–0.1Sc, Al–0.1Zr and ternary Al–0.1Sc–0.1Zr (at.%) alloys aged isochronally between 200 and 600 C. Precipitation of Al3Sc (L12) commences between 200 and 250 C in Al–0.1Sc, reaching a 670 MPa peak microhardness at 325 C. For Al–0.1Zr, precipitation of Al3Zr (L12) initiates between 350 and 375 C, resulting in a 420 MPa peak microhardness at...

Stroke welcomes Letters to the Editor and will publish them, if suitable, as space permits. Letters must reference a Stroke published-ahead-of-print article or an article printed within the past 3 weeks. The maximum length is 750 words including no more than 5 references and 3 authors. Please submit letters typed double-spaced. Letters may be shortened or edited. Include a completed copyright t...

In this research work, the possibility of semi industrial production of Al-TiB2 and Al-ZrB2 composites, using reactive slag in a flame furnace have been investigated. For this purpose, commercial pure aluminum and powder mixture of TiO2 (ZrO2) , KBF4 and Na3AlF6 were used. The results showed that using a proper ratio of slag forming materials as well as proper amounts of the above-mentioned com...

In this research work, the possibility of semi industrial production of Al-TiB2 and Al-ZrB2 composites, using reactive slag in a flame furnace have been investigated. For this purpose, commercial pure aluminum and powder mixture of TiO2 (ZrO2) , KBF4 and Na3AlF6 were used. The results showed that using a proper ratio of slag forming materials as well as proper amounts of the above-mentioned com...