Corrosion behavior of friction stir processing (FSP) WE43 alloy in a simulated body fluid (SBF) was investigated. Micro-galvanic corrosion was the dominated corrosion behavior, and the corrosion resistance of FSP WE43 alloy was improved compared to the cast counterpart. Furthermore, due to the fine-grained and homogeneous microstructure, uniform corrosion morphology was observed on FSP WE43 all...

The purpose of this study is to understand the electrochemical corrosion behavior of 1wt% Cu content Al-6Si-0.5Mg alloy in 0.1M NaCl solution. The potentiodynamic polarization curves reveal that 1wt% Cu content alloy is less prone to corrosion than the Cu free alloy. The EIS test results show that corrosion resistance or polarization resistance (Rct) increases with the addition of 1wt% Cu to Al...

The effect of long period stacking ordered (LPSO) phase and γ' precipitates on the ageing behavior and mechanical properties of the extruded Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr (wt.%) alloy was investigated. The results show that more β' phases precipitate during ageing treatment in the LPSO phase containing alloy so that the LPSO phase containing alloy exhibits a higher age-hardening response than the γ...

In this study, magnesium-zinc (Mg-Zn) alloy was investigated as a biodegradable orthopedic implant. MC3T3-E1 cell attachment, mineralization and osteogenic-specific mRNA expression were assessed for as measurements of the in vitro biocompatibility of Mg-Zn alloy. In vivo degradation of the Mg-Zn alloy and the accompanying new bone formation in the femoral marrow cavity were analyzed by scanning...

The basis for developing a new dental alloy with high Au content is appropriate chemical composition and manufacturing technology. The demands which have to be met when developing a new dental alloy are linked with fulfilling the necessary requirements for making the alloy suitable for use in metal-ceramic restorations. Due to the stress generated by masticatory forces, alloys for dental restor...

This report presents a translation from UML class diagrams [OMG15, Rum16] to Alloy modules [Jac06] and a translation from Alloy instances back to UML object diagrams. An overview of the translation was first presented in [MRR11a] and applied in [MRR11b] to semantic differencing of class diagrams. It supports an extended list of CD language features, including, e.g., directed associations, compo...

The present work demonstrates that friction stir welding (FSW) is a feasible route for joining 6061 aluminium (Al) alloy to AISI 1018 steel. The weld has a good weld quality and is free of cracks and porosity. The tensile failure happened at the boundary between the nugget and thermomechanically affected zone of the base Al alloy, indicating that the weld has a higher joining strength. Despite ...

We report quantitative measurements of the impact of alloy disorder on the ν = 5/2 fractional quantum Hall state. Alloy disorder is controlled by the aluminum content x in the Al(x)Ga(1-x)As channel of a quantum well. We find that the ν = 5/2 state is suppressed with alloy scattering. To our surprise, in samples with alloy disorder the ν = 5/2 state appears at significantly reduced mobilities w...

Ageing of 75% cold rolled Al-6Mg alloy with ternary 0.4 wt% scandium and quaternary zirconium and titanium has been carried out. Alloy samples are naturally, isochronally and isothermally aged for different time and temperatures. Hardness values of the differently processed alloys have been measured to understand the ageing behavior of Al-6Mg alloy with scandium and quaternary zirconium and tit...

This study aimed to examine the shear bond strength between cobalt chromium alloy and autopolymerizing acrylic resin using experimental primers containing 5, 10, and 15 wt% of 4-methacryloxyethyl trimellitic anhydride or 1, 2, and 3 wt% of 3-methacryloxypropyl-trimethoxysilane comparison to 5 commercial primers (ML primers, Alloy primer, Metal/Zirconia primer, Monobond S, and Monobond plus). Si...