The fatigue growth of a fiber reinforced composite laminate was characterized under thermal cycling using a combined experimental and computational investigation. Twenty-four ply composite laminates (1⁄20 12=90 12 ) are fabricated with a pre-existing delamination, and subjected to thermal cycling in an environmental chamber. The large mismatch in the coefficients of thermal expansion is used to...

Effect of holding time and temperature on the fatigue life of micro Sn-Ag-Cu solder joint has been studied with waveform of triangle and trapezoid wave at 298K and 398K. Both the microstructural coarsening and the crack propagation occurred simultaneously and therefore the cyclic load decreased rapidly in the trapezoidal wave at 398K compared with the other conditions. Therefore, under the cond...

Steels are heavily used in infrastructure and the transportation industry, and enhancing their fatigue resistance is a major challenge in materials engineering. In this study, by introducing a gradient microstructure into 304 austenitic steel, which is one of the most widely used types of stainless steel, we show that a strength gradient substantially enhances the fatigue life of the material. ...

Abstract: To ensure the rail transportations safety, evaluation of fatigue behavior of the rail steel is necessary. High cycle fatigue behaviour of a rail steel was the subject of investigation in this research using fracture mechanics. Finite element method (FEM) was used for analyzing the distribution of the stresses on the rail, exerted by the external load. FEM analysis showed that the ...

ÐThe high-temperature fatigue-crack propagation and fracture resistance of a model g-TiAl intermetallic composite reinforced with 20 vol.% ductile b-TiNb particles is examined at elevated temperatures of 650 and 8008C and compared with behavior at room temperature. TiNb reinforcements are found to enhance the fracture toughness of g-TiAl, even at high temperatures, from about 12 to 040 MPa m, a...

The fatigue crack growth in a coarse-grained Fe-2 wt% Si alloy is investigated in considerable detail. At room temperature, the material is quasi-brittle and the failure mode is mixed cleavage. Under a mode-I cyclic loading, the crack can overcome the barrier effect of grain boundaries, which dominates the overall damage evolution. Associated with the geometrically necessary crack front branchi...

Fatigue is the progressive, localized, permanent structural change that occurs in materials subjected to fluctuating stresses and strains that may result in cracks or fracture after a sufficient number of fluctuations. Fatigue fractures are caused by the simultaneous action of cyclic stress, tensile stress and plastic strain. If any one of these three is not present, fatigue cracking will not i...