A multilayer composite ceramic membrane was prepared by depositing a nano-scale layer of SiO2 on top of a modified porous alumina support by chemical vapor deposition (CVD) method. The modification of the support was carried out by adding a graded layer of Al2O3 (γ-alumina phase), using sol-gel method. An optimized temperature of 700 K for intermediate layer calcination was gained by XRD analys...

agal2o3 nanocomposite were synthesized by solution combustion technique using ammonium carbonate as a new fuel under simultaneous combustion of alumina and silver particles condition. samples prepared with different amount of silver, were characterized by xrd, bet, sem and optical absorption measurements. xrd analysis was used to determine the change in phase and size of the synthesized nanopar...

Friction stir processing was applied for fabricating an aluminum alloy based hybrid nano composite reinforced with nano sized Al2O3 and micro sized graphite particles. A mixture of Al2O3 and graphite particles was packed into a groove with 1 mm width and 4.5 mm depth, which had been cut in 5083 aluminum plate of 10 mm thick. Packed groove was subjected to friction stir processing in order to im...

Several researchers have shown that Pt-Rh bimetallic catalysts can perform synergistically for the NO/H2, NO/CO, CO/O2, and NO/CO/HC reactions [1-5]. Lakis and coworkers clarified some of the mystery surrounding the synergistic performance of Pt-Rh catalysts for the NO + H2 reaction by using analytical electron microscopy (AEM) to show that the synergistic performance of a Pt(95%)Rh(5%)/γ-Al2O3...

To understand the formation of structural isomers alumina (Al2O3) on surfaces Fe–Cr–Al alloys, cathodoluminescence (CL), X-ray photoelectron spectroscopy (XPS), and diffraction (XRD) were used. The alloys annealed under oxygen at a low partial pressure to focus initial Al2O3. XRD revealed that corundum (α-Al2O3) was predominantly formed alloy after annealing approximately 1100°C, whereas γ-Al2O...

Ammonia has been suggested as a carbon-free hydrogen source, but a convenient method for producing hydrogen from ammonia with rapid initiation has not been developed. Ideally, this method would require no external energy input. We demonstrate hydrogen production by exposing ammonia and O2 at room temperature to an acidic RuO2/γ-Al2O3 catalyst. Because adsorption of ammonia onto the catalyst is ...

The catalytic wet air oxidation (CWAO) of cationic red GTL over the Fe2O3-CeO2-Bi2O3/γ-Al2O3 catalyst was investigated under mild operating conditions in a batch reactor. The catalyst was prepared by wet impregnation, and characterized by N2 adsorptiondesorption (BET measurement), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The effect of the reaction conditions (catalyst...

Two preparation methods (wet saturation impregnation with vanadyl acetylacetonate and ball-milling of γ-Al2O3 with crystalline V2O5) were applied to produce two sets of VOx/γ-Al2O3 catalysts with increasing vanadium loadings. Materials from both sets were characterized by XRD, SEM, Raman, TPR and UV/Vis-DRS to elucidate the influence of the preparation method on the morphology of VOx species an...

In the present study, γ-Al2O3 was fabricated from Tan Rai alumina hydroxide by some following steps: purifying hydroxitde HCl solution 5% to remove impurities, dissolving 25% obtain AlCl3 and then react with (NH4)2CO3 get AACH, decomposition of AACH at 500oC produce γ-Al2O3. After that, Sodium dodecyl sulfate (SDS) used modify surface increased area. The material will be removal Rhodamine B was...