(Bi0.5L0.5)(Fe0.7Co0.3)O3 (L = La, Nd, Sm, Gd, Dy) thin films with ferromagnetism and ferroelectricity were fabricated using pulsed DC sputtering technique to obtain high saturation magnetization, perpendicular magnetic anisotropy large Kerr effect. These properties are very important for realization of performance devices driven by electric field. All had relatively Especially, (Bi0.5Nd0.5)(Fe...

nanocrystalline particles of barium hexaferrite has been prepared by the sol–gel auto- combustion method using iron and barium nitrate with a ba:fe molar ratio of 1:10. the effect of fuel such as citric acid and aspartic acid was investigated on the structure and magnetic properties of nanoparticles. the results revealed that the formation of barium hexaferritefine particles is influenced by mo...

Obtaining high magnetization sputtered thin films with soft properties requires small grains with good exchange coupling between the grains. Contamination of grain boundaries during deposition will significantly degrade magnetic softness and reduce magnetization. In this paper, we report on such contamination induced by substrate bias during sputter deposition of Fe35Co65 films. 100-nm-thick Fe...

We have demonstrated the synthesis of γ-Fe2O3 nano-particles through a facile and novel calcination process in the air. There is no pH regulation, gas atmosphere, additive, centrifugation or other complicated procedures during the preparing process. A detailed formation process of the nano-particles is proposed, and DMF as a polar solvent may slower the reaction process of calcination. The stru...

Ordered CoNiP nanowires with the same length of 4 µm and varying diameters (d = 100 nm-600 nm) were fabricated by electrodeposition of CoNiP onto polycarbonate templates. X-ray diffraction, scanning electron microscopy, and high-resolution transmission electron microscopy confirmed the quality of the fabricated nanowires. Magnetic measurements and theoretical analysis revealed that the magnetiz...

despite providing robustness, high-gain observers impose a peaking phenomenon, which may cause instability, on the system states. in this paper, an adaptive saturation is proposed to attenuate the undesirable mentioned phenomenon in high-gain observers. a real-valued and differentiable sigmoid function is considered as the saturating element whose parameters (height and slope) are adaptively tu...

(Fe0 7Co0 3)1 N (or FeCoN) alloy single layers and FeCoN film sandwiched between two very thin (5 nm) permalloy layers have been synthesized by RF diode sputtering. The saturation magnetization of the as-deposited FeCoN single layers was found to be around 24.5 kG, the same as the pure Fe0 7Co0 3 alloy; and the minimum hard-axis coercivity was 5 Oe. In contrast, the sandwiched FeCoN films have ...

magnetic nanoparticles are the good choice for using in mri as the contrast agent. iron oxide particles such as magnetite (fe3o4) or its oxidized form maghemite (γ-fe2o3) are the most commonly employed in biomedical applications. in this study, we synthesized and optimized the preparation of chitosan manganese-ferrite nanoparticles (cmn-fe nps) and evaluated its ability for the mice macrophage ...

A thin FePt film was deposited onto a CrV seed layer at 400°C and showed a high coercivity (~3,400 Oe) and high magnetization (900-1,000 emu/cm(3)) characteristic of L 10 phase. However, the magnetic properties of patterned media fabricated from the film stack were degraded due to the Ar-ion bombardment. We employed a deposition-last process, in which FePt film deposited at room temperature und...

Based on a low-temperature route, monodispersed CoFe(2)O(4) microspheres (MSs) were fabricated through aggregation of primary nanoparticles. The microstructural and magnetic characteristics of the as-prepared MSs were characterized by X-ray diffraction/photoelectron spectroscopy, scanning/transmitting electron microscopy, and vibrating sample magnetometer. The results indicate that the diameter...