In mode II interlaminar fracture toughness tests of composite laminates, the evaluated based on linear elastic mechanics deviates from true due to material nonlinearity matrix. this study, an elastoplastic finite-element analysis was performed a new quasi-static test, i.e., doubly end-notched tension (DENT) investigate difference between perceived energy release rate and J-integral. The effect ...

This study was conducted to determine whether novel experimental low-shrinkage dimethacrylate co-monomers could provide low polymerization shrinkage composites without sacrifice to degree of conversion, and mechanical properties of the composites. Experimental composites were prepared by mixing 28.6 wt% of bisphenol-A-glycidyl dimethacrylate based resin matrix (bis-GMA) with various weight-frac...

Few studies have focused on a description of the fracture toughness properties of dentin in terms of resistance-curve (R-curve) behavior, i.e., fracture resistance increasing with crack extension, particularly in light of the relevant toughening mechanisms involved. Accordingly, in the present study, fracture mechanics based experiments were conducted on elephant dentin in order to determine su...

BACKGROUND/AIM Fracture toughness determines functional crown strenght and prevents damages on ceramics during mastication. There is a lack of relevant literature data about fracture toughness of crowns made by feather-edge preparation. Mechanical testing of ceramic samples is supposed to show if feather-edge tooth preparation is a successful method for making ceramic crowns without any risk of...

statement of problem: tooth-coloured restorative materials are brittle with the major shortcomings of sensitivity to flaws and defects. although various mechanical properties of resin composites have been studied, no fracture toughness test data for nano-hybrid composites under acidic condition for a long period of time has been published. objectives: to compare the fracture toughness (k ic ) o...

changes in moisture content and temperature can perturb both stiffness and strength and as such the impact resistance of composite structures. in this paper, the pre-notched basalt fibre reinforced epoxy (bfre) composite specimens are studied under charpy impact loads in order to investigate the changes in impact energy absorption (fracture toughness) with different kinds of aging conditions. t...

BACKGROUND Polymer infiltrated ceramics and nano-ceramic resins are the new restorative materials which have been developed in order to enhance the adverse properties of glass-matrix ceramics and resin composites. The aim of the present in vitro study was to evaluate the characteristics of various CAD/CAM materials through mechanical, microstructural, and SEM analysis. METHODS Five test group...

The proportional relationships between the Charpy absorbed energy (CVN) and the KIC values have been established for a wide variety of steels. Several formulae have been proposed that predict KIC from CVN. The purpose of this study is to investigate, by means of compact testing fracture toughness specimens, the effective role of microstructure for estimation of the fractur...

Final failure of laminated composite structures is preceded by different damage mechanisms involving fracture initiation and propagation. Fracture in a composite laminate can appear either between two plies or within a lamina. In the first case, interlaminar fracture or delamination, the crack causes separation of two adjacent plies and will mainly involve matrix failure or matrix-to-fibre debo...