نتایج جستجو برای: fatigue crack

تعداد نتایج: 89334  

2014
ARTHUR J McEVILY ROBERT P WEI A. J. McEvily R. P. Wei

The development and current state-of-the-art in fracture mechanics in relation to studies of environment-enhanced fatigue-crack growth (corrosion fatigue) and fatigue-crack growth per se are reviewed. Patterns of response of materials to different loading and environmental conditions are considered in terms of the probable mechanisms for environmental embrittlement. The usefulness of the fractu...

2011
David Gustafsson

In this licentiate thesis the work done in the TURBO POWER project Influence of high temperature hold times on the fatigue life of nickel-based superalloys will be presented. The overall objective of this project is to develop and evaluate tools for designing against fatigue in gas turbine applications, with special focus on the nickel-based superalloy Inconel 718. Firstly, the constitutive beh...

2012
Yoshimitsu Okazaki

The fatigue strength, effects of a notch on the fatigue strength, and fatigue crack growth rate of Ti-15Zr-4Nb-4Ta alloy were compared with those of other implantable metals. Zr, Nb, and Ta are important alloying elements for Ti alloys for attaining superior long-term corrosion resistance and biocompatibility. The highly biocompatible Ti-15Zr-4Nb-4Ta alloy exhibited an excellent balance between...

Journal: :international journal of advanced design and manufacturing technology 0
rahmatollah ghajar department of mechanical engineering khajehnasir toosi university javad alizadeh

in the last decade, decrease of the wear rate, increase in the axel load, and the velocity of the trains have changed the main damage mechanism of railway wheels from wear to rolling contact fatigue (rcf). rcf may lead to surface and subsurface cracks. the interaction between wear and rcf, removes the surface cracks, but the subsurface crack propagate gradually, and may lead to deeper and more ...

2005
Shih-Yu Liu

Uniaxial tension-compression fatigue behavior of 3-mol%yttria-stabilized tetragonal zirconia polycrystals was investigated. Hysteresis in the stress-plastic strain curve featured cumulative plastic strain and weakened elastic stiffness. Fracture statistics in terms of cycle-to-failure depends strongly on the maximum stress and less on the stress amplitude. Preexisting processing flaws were iden...

2014
Longgang Tian Leiting Dong Nam Phan Satya N. Atluri

In the present paper, stress intensity factor (SIF) analyses and fatigue-crack-growth simulations of corner cracks emanating from loaded pinholes of attachment lugs in structural assemblies are carried out for different load cases. A three-dimensional (3D) symmetric Galerkin boundary-element method (SGBEM) and FEM alternating method is developed to analyze the nonplanar growth of these surface ...

This experimental study investigated the effects of quenching and tempering heat treatment on fatigue behavior and also tempering temperature and time holding of AISI 1060 steel. At first, the specimens were austenitized at 800˚C for 1 hour, and then were quenched in the water bath of 25˚C temperature. After that, tempering process was done at the temperature of 250˚C, 450˚C and 650˚C for 1 and...

2016
Nicholas A. Nechval Vadims Danovics Natalija Ribakova

The main aim of this paper is to present more accurate stochastic fatigue models for solving the fatigue reliability problems, which are attractively simple and easy to apply in practice for situations where it is difficult to quantify the costs associated with inspections and undetected cracks. From an engineering standpoint the fatigue life of a structure consists of two periods: (i) crack in...

2006
T. Connolley P. A. S. Reed M. J. Starink

The natural initiation and growth of short cracks in Inconel 718 U-notch specimens has been studied at 600C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1...

2014
Xi-Shu Wang Xing-Wu Guo Xu-Dong Li Dong-Yun Ge

In this paper, rotating bending fatigue tests of 2024-T4 Al alloy with different oxide coatings were carried out. Compared to the uncoated and previously reported oxide coatings of aluminum alloys, the fatigue strength is able to be enhanced by using a novel oxide coating with sealing pore technology. These results indicate that the better the coating surface quality is, the more excellent the ...