Wear of elements subjected to friction and sliding is among the main causes of low tribological performance and short lifetime of strategic materials such as titanium alloys. These types of alloys are widely used in different areas such as aerospace and the biomechanics industry. In this sense, surface modification treatments allow for the overcoming of limitations and improvement of features a...

Torsional fretting behavior of TC4 titanium alloy has been investigated at different parameters to explore the wear resistance and mechanisms alloy. The loops, dissipated friction energy torque under normal load (100N 200N), angular displacement (±0.5° ±2°) frequency (10Hz 15Hz) were studied reveal mechanical during fretting. Results showed that made difference in while was most important facto...

Fretting wear is the material damage of two contact surfaces caused by micro relative displacement. Its characteristic is that debris is trapped on the contact surfaces. Depending on the material properties, the shapes of the debris, and the dominant wear mechanisms, debris can play different roles that either protect or harm interfaces. Due to the micro scale of the debris, it is difficult to ...

In this study, the friction and wear behavior of ultrahigh molecular weight polyethylene (UHMWPE) were evaluated as a function of polymer crystallinity in the presence of the phospholipid dipalmitoyl phosphatidylcholine (DPPC) dissolved in ethanol. Samples of UHMWPE were separately heat treated to get high and low crystallinity samples. Degree of crystallinity was evaluated using differential s...

Historically, the study of the wear of hard dental tissues in modern man has been limited to clinical observation of physiologic and pathologic conditions that lead to wear, and to attempts to duplicate the effects of hygienic procedures such as the use of toothbrush and dentifrice on hard dental tissues in the laboratory. However, several fundamental investigations have been reported in which ...

The effect of the milling time & ageing on the hardness, density, and wear characteristics of Al 7150 alloy specimens made via powder metallurgy has been studied. The different constituents of Al 7150 alloy were processed in a planetary ball milling set up with a BPR of 10:1 for 5 hours, 10 hours, and 20 hours. At 400 °C, the milled powders were subsequently hot compacted in a punch die setup. ...

An anti-friction Babbitt alloy-coated bearing made by a casting process is a journal bearing, which is used in an ore cone crusher eccentric. The main purpose of the Babbitt coated eccentric is to provide a low friction to support and guide a rotating shaft. Despite the fact that the Babbitt-coated eccentric offers a low friction coefficient and can be operated without a continuous supply of lu...

In this investigation, MoSx/Cr coatings were deposited by direct-current magnetron sputter onto Ck45 (AISI 1045) plain carbon steel substrates. The MoSx/Cr ratio in the coatings was controlled by sputtering the composite targets. The chemical characterization was performed using EDX (energy dispersive X-ray analysis); the structural characterization was accomplished by X-ray diffraction (XRD) s...