A simple, robust and versatile hydrothermal synthesis route to in situ functionalized TiO2 nanoparticles was developed using titanium(IV) isopropoxide as Ti-precursor and selected silane coupling agents (3-aminopropyltriethoxysilane (APTES), 3-(2-aminoethylamino)propyldimethoxymethylsilane (AEAPS), and n-decyltriethoxysilane (DTES)). Spherical nanoparticles (ca. 9 nm) with narrow size distribut...

TiO2 composites with zeolite templated carbon (TiO2-ZTC) and activated carbon (TiO2-AC) were prepared and used as the photocatalysts for comparative studies with pure TiO2. TiO2-ZTC exhibited the highest rate of methylene blue degradation with a rate approximately 4 and 400 times higher than those of TiO2-AC and pure TiO2, respectively. Moreover, the highest catalytic performance of TiO2-ZTC in...

zno nanowires with a diameter of 70 nm and nanorods with a diameter in the range of 100-150 nm and two micrometer in length were grown on glass substrates by resistive evaporation method and applying a two step oxidation process at low temperatures, without using any catalyst, template or buffer layer. xrd pattern of these nanostructures indicated a good crystallinity property with wurtzite hex...

Nanocomposites based on TiO2-supported copper nanoparticles were prepared by a hydrothermal method where copper nanoparticles with or without the passivation of 1-decyne were chemically grown onto TiO2 nanocolloid surfaces (and hence denoted as CuHC10/TiO2 and Cu/TiO2, respectively). Transmission electron microscopy measurements showed that the size of the hybrid nanoparticles was 5-15 nm in di...