Abstract Ductile damages often happen on metal structures under large deformations. In the current paper, ductile damage criteria are discussed from microscopic mechanism to fracture models. Abaqus FEA makes easy be applied for practical problems. Therefore, paper finally presents detailed implementation of in describe and degradation, simulating failure process with higher fidelity.
T1B2 and CeO2 particle-reinforced A16061 hybrid composites were manufactured using stir casting hot rolling techniques. The base alloy hot-rolled at 500°C a 50% reduction was achieved through 12 passes. effect of varying TB2 particle additions on the microstructure mechanical properties Al6061 matrix studied. Scanning electron microscopy showed uniform dispersion both reinforcements, with good ...
Impact tests are mandatory for a wide range of structural steel products to evaluate the required service life and operational safety. This test is especially relevant used in operation climatic areas with cold climate, since it allows one determine temperature ductile-brittle transition. Depending on structural-phase state metal, type relationship impact toughness its displacement axis may dif...
The failure due to accidental drop of magnetic recording disks made of brittle or ductile materials is of great interest in the design of small form factor hard disk drives. In this study, fracture of glass disks (brittle material) and plastic deformation of aluminum disks (ductile material) at very high shock levels caused by accidental drop are investigated using finite element analysis. It i...
The influence of a minor strontium (Sr) modifier on the microstructures and mechanical properties of 7075 Al alloys was investigated in this paper. The grain size of cast 7075 Al alloys was refined from 157 μm to 115 μm, 108 μm, and 105 μm after adding 0.05 wt. %, 0.1 wt. %, and 0.2 wt. % Sr, respectively. The extruded 7075 Al alloys was refined with different degrees of Sr modifier. The mechan...
This research was carried out to investigate the influence of Sr-Sb on the microstructures and mechanical properties of Al-18 wt % Mg₂Si-4.5Cu alloys. After the addition of 0.2 wt % Sr-Sb, the morphologies of primary Mg₂Si transformed from equiaxed dendrite to cube in as-cast alloys and the average size of primary Mg₂Si decreased from ~50 to ~20 μm. The shape of eutectic Mg₂Si changed from Chin...
Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...
ÐThe high-temperature fatigue-crack propagation and fracture resistance of a model g-TiAl intermetallic composite reinforced with 20 vol.% ductile b-TiNb particles is examined at elevated temperatures of 650 and 8008C and compared with behavior at room temperature. TiNb reinforcements are found to enhance the fracture toughness of g-TiAl, even at high temperatures, from about 12 to 040 MPa m, a...
The relationship between composition, structure, and resistance to fracture remains poorly understood. Here, based on molecular dynamics simulations, we report that 1 sodium silicate glasses (NS) and calcium–silicate–hydrates (CSH) feature an anomalous maximum in fracture toughness. In the framework of topological constraint theory, this anomaly is correlated to a flexible-to-rigid transition, ...