This in vitro study evaluated the temperature of dentures after different microwave irradiation protocols. Two complete dentures (one maxillary and one mandibular denture) were irradiated separately 4 times for each of the following 5 protocols: dentures immersed in water (G1- 6 min, G2- 3 min); dentures kept dry (G3- 6 min); dentures placed in the steam sterilizer (G4- 6 min, G5- 3 min). The f...

STATEMENT OF PROBLEM Increasing the thickness of intraoral autopolymerizing hard denture base liners may result in a temperature rise and a burning sensation for patients. PURPOSE The purpose of the study was to determine whether increasing the thickness of hard autopolymerizing reline resin increases the temperature of the basal seat area of a denture during the polymerization process. MAT...

Background and aims. The aim of this study was to compare flexural strength of specimens processed by conventional and injection-molding techniques. Materials and methods. Conventional pressure-packed PMMA was used for conventional pressure-packed and injection-molded PMMA was used for injection-molding techniques. After processing, 15 specimens were stored in distilled water at room temperatur...

The aim of this study was to evaluate the dimensional changes of denture bases made from different resins after different storage periods. For this purpose, 25 sets of plaster models/resin bases were prepared using 4 acrylic resins submitted to two types of polymerization: 1--QC-20 submitted to polymerization by microwave energy; 2--QC-20 submitted to polymerization by water hot bath; 3--Vipi C...

objective: the purpose of this study was to evaluate the transverse strength of one brand of denture base material repaired with two autopolymerized acrylic resins with and without wire reinforcement. materials and methods: eighty samples (2.5×10×65 mm3) were fabricated and divided into five groups. the control group was left intact. groups b and d specimens were repaired with autopolymerizing ...

PURPOSE This study assessed the shear bond strength of 4 hard chairside reline resins (Kooliner, Tokuso Rebase Fast, Duraliner II, Ufi Gel Hard) to a rapid polymerizing denture base resin (QC-20) processed using 2 polymerization cycles (A or B), before and after thermal cycling. MATERIALS AND METHODS Cylinders (3.5 mm x 5.0 mm) of the reline resins were bonded to cylinders of QC-20 polymerize...

BACKGROUND Fractures of acrylic resin dentures are a common occurrence in clinical dentistry. The denture may be fractured accidentally when dropped or while in service in the mouth due to flexural fatigue. OBJECTIVES The aim of this study was to compare the elastic modulus and the flexural strength between two heat-cured acrylic resins used in denture bases: a high-impact resin (Lucitone 199...

Purpose: The purpose of this study was to determine the influence of silicone remover on tensile bond strength of eight silicone-resilient denture liners to a denture base resin. Durability of bond strength of resilient denture liner to denture base resin was also examined by thermal cycling test. Materials and Methods: Eight commercial silicone resilient denture liners were used. The specimens...