This study investigated experimentally the fracture properties, i.e., the fatigue strength, the resistance to crack propagation and the fracture toughness, of an acrylic bone cement (Cemex RX). The mean endurance limit was determined following the staircase method. The endurance limit was estimated at 9.2 MPa. The fatigue crack propagation rate was measured according to the ASTM E647 standard. ...

In this work, the plastic deformation mechanisms responsible for mechanical properties and fracture toughness in nanotwinned (NT) magnesium is studied by molecular dynamics (MD) simulation. The influence of twin boundary (TBs) spacing and crack position on deformation behaviors are investigated. The microstructure evolution at the crack tip are not exactly the same for the left edge crack (LEC)...

An important task in mixed-mode fracture analysis and prediction is the simulation of crack growth under mixed-mode conditions. To complete such a task, one must have (a) a computer code capable of handling the kinematics of general crack growth and determining the stress and deformation states during crack growth, and (b) a fracture criterion that can properly predict the instant and direction...

ÐFatigue crack initiation and multiplication of the unnotched SCS-6 silicon carbide ®ber-reinforced titanium matrix composites with di€erent matrix and interfacial properties have been investigated experimentally and analytically. Ti±15V±3Al, Ti±6Al±4V, and Ti±22Al±23Nb were chosen as matrix materials. The initiation and propagation of each individual matrix crack as a function of fatigue cycle...

In this master thesis, work done in the TURBO POWER project High temperature fatigue crack propagation in nickel-based superalloys during spring 2012 will be presented. The overall objective of this project is to develop and evaluate tools for designing against fatigue in gas turbine applications, with special focus on the crack propagation in the nickel-based superalloy Inconel 718. Experiment...

The corrosion fatigue crack growth characteristics of small (>35pm) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500X) crack length measurements in laboratory air and 1% NaCl environments. To quantify the “small crack effect” in the corrosive environment, the corrosion fatigue crac...

The growth of slant cracks by fretting fatigue of a half plane in contact with a flat rounded pad was studied. The mode I and mode II stress intensity factors for cracks of various lengths and directions were calculated using the semi-analytical method of the distribution of dislocations, and their cumulative effect on the crack growth was investigated using the strain energy density criterion....

RESTRICTIONS on the quasi-static extension, or healing, of Griffith cracks are developed in the framework of irreversible thermodynamics. It is emphasized that thermodynamics requires that (G 2r)I > 0, where i is crack speed, G the Irwin energy release rate, and 2y the work of reversible separation of the surfaces to be fractured. Implications for ‘lattice trapping’ models of cracks and for the...

Precracked and notched specimens were used to investigate the fracture mechanism of a bainite steel at low temperature. The critical fracture event was studied using metallographic sectioning method. The results showed that the critical cleavage event was different in the precracked and the notched specimens. At -196C, all specimens fractured at lower-shelf region without any ductile crack grow...

An infinite elastic medium with a planar crack is considered. The crack is subjected to the pressure of fluid injected at a point on the crack surface. Description of the crack growth is based on the lubrication equation (balance of the injected fluid and the crack volume), the equation for crack opening caused by fluid pressure on the crack surface, the Poiseuille equation related local fluid ...