External sulfate attack of concrete is a major problem that can appear in regions where concrete is exposed to soil or water containing sulfates, leading to softening and cracking of the concrete. Therefore, it is important that materials selection and proportioning of concrete in susceptible regions be carefully considered to resist sulfate attack. American Society for Testing Materials (ASTM)...

This data article provides a comparison data for nano-cement based concrete (NCC) and ordinary Portland cement based concrete (OPCC). Concrete samples (OPCC) were fabricated using ten different mix design and their characterization data is provided here. Optimization of curing time using the Weibull distribution model was done by analyzing the rate of change of compressive strength of the OPCC....

Here, the development of an adhesive is reported - generated via free radical polymerization - which can be degraded upon thermal impact within minutes. The degradation is based on a stimuli responsive moiety (SRM) that is incorporated into the network. The selected SRM is a hetero Diels-Alder (HDA) moiety that features three key properties. First, the adhesive can be degraded at relatively low...

BACKGROUND There are several vacuum mixing systems on the market which are arbitrarily used with various bone cements in clinical work. Hardly any studies have been done on the performance and handling of these systems in combination with different cement brands. MATERIAL AND METHODS We therefore tested 6 vacuum mixing systems (Palamix, Summit, Cemvac, Optivac, Vacumix, MixOR) in combination ...

Calcium aluminate cement (CAC) suffers from loss of workability in less than an hour (~15 minutes) after first touch of water. Current superplasticizers that are utilized to modify the viscosity of cement admixtures are designed to target ordinary Portland cement (OPC). The high affinity between these superplasticizers and cement particles were found to be detrimental in CAC systems. Utilizatio...

OBJECTIVE The aim of this study was to evaluate the shear bond strength (SBS) of brackets bonded to demineralized enamel pretreated with low viscosity Icon Infiltrant resin (DMG) and glass ionomer cement (Clinpro XT Varnish, 3M Unitek) with and without aging. METHODS A total of 75 bovine enamel specimens were allocated into five groups (n = 15). Group 1 was the control group in which the enam...

The aim of this study was to investigate the compressive strength and surface roughness of two glass ionomer cements and two resin-based fissure sealants before and after fluoride release and recharge. Twenty-one specimens were prepared and divided into three groups for each material. First group was loaded in compression until failure. Fluoride released was measured from the remaining specimen...

We have succeeded in improving the material properties of a chelate-setting calcium-phosphate cement (CPC), which is composed of hydroxyapatite (HAp) the surface of which has been modified with inositol hexaphosphate (IP6) by adding α-tricalcium phosphate (α-TCP) powder. In order to create a novel chelate-setting CPC with sufficient bioresorbability, gelatin particles were added into the IP6-HA...

introduction: the purpose of this study was to compare the push-out bond strength of white proroot mineral trioxide aggregate (mta), biodentine, calcium-enriched mixture (cem) cement and endosequence root repair material (errm) putty after exposure to blood. methods and materials: a total of 96 root dentin slices with a standardized thickness of 1.00±0.05 mm and standardized canal spaces were r...

This study reports for the first time in vitro and in vivo properties of fluorapatite (FA)-forming calcium phosphate cements (CPCs). The experimental cements contained from (0 to 3.1) mass % of F, corresponding to presence of FA at levels of approximately (0 to 87) mass %. The crystallinity of the apatitic cement product increased greatly with the FA content. When implanted subcutaneously in ra...