CoTe and CoTe2 nanorods with average diameter of 100 nm were synthesized by a simple hydrothermal process, and different CoTe2 nanostructures were obtained by changing the NaOH concentration. CoTe nanorods exhibit weak ferromagnetism while CoTe2 nanorods present paramagnetic behavior. Different magnetic behaviors occur in the other CoTe2 nanostructures due to Na+ entrance into CoTe2 crystals. A...

Gold nanorods have been synthesized by photochemically reducing gold ions within a micellar solution. The aspect ratio of the rods can be controlled with the addition of silver ions. This process reported here is highly promising for producing uniform nanorods, and more importantly it will be useful in resolving the growth mechanism of anisotropic metal nanoparticles due to its simplicity and t...

The formation process of titania based nanorods during hydrothermal synthesis starting from an amorphous TiO2.nH2O gel has been investigated. Sodium tri-titanate (Na2Ti3O7) particles with a rodlike morphology were prepared by a simple hydrothermal process in the presence of a concentrated NaOH aqueous solution. The ion exchange reaction of the synthesized Na2Ti3O7 nanorods with HCl under ultras...

Semiconductor TiO2 photocatalysis has attracted much attention due to its potential application in solving the problems of environmental pollution. In this paper, thiourea (CH4N2S) modified anatase TiO2 nanorods were fabricated by calcination of the mixture of TiO2 nanorods and thiourea at 600 °C for 2 h. It was found that only N element was doped into the lattice of TiO2 nanorods. With increas...

Control of the size of Cu nanorods vapor-deposited at an oblique angle (approximately 85 degrees) by oxygen-mediated growth was investigated using scanning electron microscopy (SEM) and x-ray diffraction (XRD). It was observed that exposure of Cu nanorods to the oxygen ambient periodically resulted in a reduction in the diameter of the nanorods as well as an increase in the areal density of the...

The determination of biogenic amines in alcoholic beverages is important to assess the potential risks associated with the consumption of high concentrations of these compounds. In addition, product storage conditions and the length of storage can cause the formation of biogenic amines that reduce product quality. We report a new method using cation-exchange chromatography with either suppresse...

A place exchange reaction between 11-mercaptoundecanoic acids (MUA) and cetyltrimethylammonium bromide (CTAB)-protected gold nanorods (GNRs) was conducted inside an ionic exchange resin; this modification resulted in functional gold nanorods soluble in both polar and nonpolar organic solvents.

Tungsten trioxide nanorods have been generated by the thermal decomposition (450 C) of tetrabutylammonium decatungstate. The synthesized tungsten trioxide (WO3) nanorods have been characterized by XRD, Raman, SEM, TEM, HRTEM and cyclic voltammetry. High resolution transmission electron microscopy and X-ray diffraction analysis showed that the synthesized WO3 nanorods are crystalline in nature w...

Hydroxyl free zinc oxide nanorods have been synthesized by a catalyst free surfactant based one-step solid state reaction process. The powder X-ray diffraction studies reveal well defined wurtzite peaks due to crystalline ZnO, while optical absorption spectra represent prominent exciton absorption and remarkable blueshift in the onset of absorption. As predicted by transmission electron microsc...

BACKGROUND Although most reported biogenic Mn oxides are hexagonal birnessites, other types of biogenic Mn oxides also commonly occur in the environment. However, sorption characteristics and underlying mechanisms of the adsorption of heavy-metal ions on these biogenic Mn oxides are still rarely addressed. In this study, the sorption mechanisms of Cu(II) on a low valence biogenic Mn oxide, poor...