In this study different nanofluids with phase change behavior were developed by mixing a molten salt base fluid (KNO3 selected as phase change material) with nanoparticles using the direct synthesis method. The thermal properties of the nanofluids obtained were investigated. Following the improvement in the specific heat achieved, these nanofluids can be used in concentrating solar plants with ...

The effect of impregnation sequence on the formation of Pt/Ni bimetallic nanoparticles supported on g-Al2O3 was investigated for catalysts with Pt/Ni atomic ratios of 3/1 and 1/1. These bimetallic catalysts were prepared with a fixed Pt loading (5 wt.%) by incipient impregnation of one metal precursor and calcination, followed by the impregnation of the second metal precursor and a second calci...

Al2O3:SiOC nanocomposites were synthesized by thermal treatment of fumed alumina nanoparticles modified by phenyltrimethoxysilane. The effect of annealing temperature in inert ambient on structure and photoluminescence of modified alumina powder was studied by IR spectroscopy as well as photoluminescence spectroscopy with ultraviolet and X-ray excitation. It is demonstrated that increase of ann...

Fuel oil has a deficit every year. Therefore, substitute fuel is needed, which can be obtained more efficiently. One of the alternative fuels that have been widely researched biofuel. Catalytic cracking method producing biofuels such as biogasoline (C5-C9), bioavtur (C10-C15) and green diesel (C16-C22). This research aims to produce by catalytic palm using HCl/γ-Al2O3 HCl/Ni/γ-Al2O3 catalysts (...

Numerical simulation and experimental investigation were used for study of laminar forced convective heat transfer of Al2O3/water nanofluid. Single phase model with temperaturedependent properties was employed for numerical simulation of transport phenomena in nanofluid. The results of experiments and computer-aided simulation indicated remarkable enhancement of convective heat transfer of base...

Coatings prepared from nanosized powders were obtained by spraying ethanol-based colloidal solutions into a plasma plume. The powders investigated included 40 nm γ -Al2O3, 75 nm 8 wt% Y2O3-ZrO2, and 750 nm 25 wt% CeO2-ZrO2. Spray distances from approximately 50 to 63 mm were required to achieve significant coating deposition. As observed in the TEM, the typical lamella morphology of air plasma ...

Experimental investigation of heat transfer during pool boiling of two nanofluids, i.e., water-Al2O3 and water-Cu has been carried out. Nanoparticles were tested at the concentration of 0.01%, 0.1%, and 1% by weight. The horizontal smooth copper and stainless steel tubes having 10 mm OD and 0.6 mm wall thickness formed test heater. The experiments have been performed to establish the influence ...

ni2+ supported on hydroxyapatite-core@shell γ-fe2o3 nanoparticles (γ-fe2o3@hap-ni2+) was found to be a useful catalyst for the synthesis of benzimidazole derivatives from o-phenylenediamine and aldehydes under solvent and solvent-free conditions at 80 °c. this reaction affords the corresponding benzimidazole derivatives compared with the classical reactions this method consistently gives a high...

V2O5 xerogel films were fabricated by casting V2O5 sols onto fluorine-doped tin oxide glass substrates at room temperature. Five, ten and twenty atomic layers of Al2O3 were grown onto as-fabricated films respectively. The bare film and Al2O3-deposited films all exhibited hydrous V2O5 phase only. Electrochemical impedance spectroscopy study revealed increased surface charge-transfer resistance o...

In this study we present new data for the thermal conductivity enhancement in four nanofluids containing 11, 25, 50, and 63 nm diameter Aluminum oxide (Al2O3) nanoparticles in distilled water. The nanofluids were prepared using single step method (that is, by dispersing nanoparticle directly in base fluid) which was gathered in ultrasonic device for approximately 7 h. The transient hot-wire las...