Magnetic nanoparticles are frequently coated with SiO2 to improve their functionality and bio-compatibility in a range of biomedical and polymer nanocomposite applications. In this paper, a scalable flame aerosol technology is used to produce highly dispersible, superparamagnetic iron oxide nanoparticles hermetically coated with silica to retain full magnetization performance. Iron oxide partic...

Fe2O3/ZSM-5 modified with Ce via citrate route (sol-gel approach) is applied for H2S removal in 500–700 ◦C temperature range. The sulfidation activity of Fe2O3/ZSM-5 is appreciably promoted by introduction of Ce plausibly attributed to the synergy of Fe2O3 and CeO2. 5Fe5Ce/ZSM-5 performs the optimal desulfurization behavior at 600 ◦C with sulfur capacity of 1020 μmol S/g, and the sulfidation pr...

Although chemically very simple, Fe2O3 is known to undergo a series of enigmatic structural, electronic and magnetic transformations at high pressures and high temperatures. So far, these transformations have neither been correctly described nor understood because of the lack of structural data. Here we report a systematic investigation of the behaviour of Fe2O3 at pressures over 100 GPa and te...

We have investigated the role of the grain boundary on the resistive magnetodielectric property of polycrystalline γ -Fe2O3 through impedance spectroscopy measurements. Depending on the sample preparation temperature, the dielectric constant of γ -Fe2O3 is significantly different especially at low frequencies (<104 Hz) and high temperatures (>200 K). The value of the magnetodielectric effect at...

The lifetimes of nonfixed holograms in LiNbO3:Fe crystals with doping levels of 0.05, 0.138, and 0.25 wt % Fe2O3 have been measured in the temperature range from 30 to 180 °C. The time constants of the dark decay of holograms stored in crystals with doping levels of 0.05 and 0.25 wt % Fe2O3 obey an Arrhenius-type dependence on absolute temperature T, but yield two activation energies: 1.0 and 0...

We present a different strategy for synthesizing the Au-γ-Fe2O3 bifunctional nanoparticle by using a larger (50 nm) Au nanoparticle as the core surrounded by smaller (10 nm) γ-Fe2O3 nanoparticles. The synthesis of the composite nanoparticles is quite facile based on a simple redox process whereby Fe2+ is used to reduce Au3+. The morphology and composition of the product is measured by transmiss...

The effect of a thin α-Fe2O3 compact buffer layer (BL) on the photoelectrochemical performances of a bare α-Fe2O3 nanorods photoanode is investigated. The BL is prepared through a simple spray deposition onto a fluorine-doped tin oxide (FTO) conducting glass substrate before the growth of a α-Fe2O3 nanorods via a hydrothermal process. Insertion of the hematite BL between the FTO and the nanorod...

Electronic structures of the vanadium/vanadium-oxide films supported on α-Fe2O3(0001) were studied by using X-ray photoemission spectroscopy. The vanadium films were grown by evaporation of metallic vanadium at room temperature. The as-deposited V had a 3+ oxidation state and the α-Fe2O3(0001) surface was reduced at the initial coverage. After complete reduction of interface iron atoms, metalli...

Nanomaterials such as iron oxides and ferrites have been intensively investigated for water treatment and environmental remediation applications. In this work, hollow α-Fe2O3 nanofibers made of rice-like nanorods were successfully synthesized via a simple hydrothermal reaction on polyvinyl alcohol (PVA) nanofiber template followed by calcination. The crystallographic structure and the morpholog...

This paper reports the synthetic route of 3-D network shape α-Fe2O3 from aqueous solutions of iron precursor using a non-ionic polymeric soft-template, Pluronic P123. During the synthesis of α-Fe2O3, particle sizes, crystal phases and morphologies were significantly influenced by pH, concentrations of precursor and template. The unique shape of worm-like hematite was obtained only when a starti...