introduction: the aim of this in vitro study was to determine the sealing ability of orthograde proroot mineral trioxide aggregate (mta) and calcium enriched mixture (cem) cement as root-end filling materials. materials and methods: fifty four extracted single-rooted human teeth were used. the samples were randomly divided into 3 experimental groups. in group a and b, 4 mm of wmta and cem cemen...

introduction: the purpose of this in vitro study was to investigate the influence of 5.25% sodium hypochlorite (naocl) and 0.12% chlorhexidine gluconate (chx) use separately and combined as endodontic irrigants on the apical sealing ability of two endodontic sealers. materials and methods: eighty-six extracted maxillary central incisor teeth were used. the teeth were decoronated at the cej, acc...

introduction: recently, attention has been drawn to the influence of smear layer removal on apical seal, and the relation of root canal filling material with canal wall surface in the presence and absence of the smear layer. the purpose of this study was to evaluate the influence of the smear layer removal on the apical sealing ability of ah26 sealer. materials and methods: forty extracted huma...

Introduction: This study compared the apical sealing ability of a bioceramic based root canal repair filling material (iRoot FS) with mineral trioxide aggregate (MTA). Methods and materials: Forty single-canal teeth were prepared and randomly divided into two experimental groups (n=18) and two control groups (n=2). Teeth in experimental groups were retrofilled with either MTA or iRoot FS. After...

The objective of this study was to compare the sealing ability of ActiV GP/glass ionomer (GI) sealer (Brasseler USA, Savannah, GA), Resilon/Epiphany (Pentron Clinical Technologies, Wallingford, CT), and gutta-percha (GP)/AH Plus (Dentsply Maillefer, Tulsa, OK). Seventy-three human single-rooted teeth were randomly divided into three test groups (20 canals each) and two control groups (5 positiv...

We investigated the use of India ink as an indicator of root canal sealing ability. Sealing ability is one of the most important factors required of root canal cements. Various dyes have been used for this purpose. Methylene blue, radioisotopes and India ink have all been tried. However, there is no evidence that India ink is suitable as an indicator. We measured the particle size distribution ...

The emergence of Mineral Trioxide Aggregate (MTA) as endodontic repair filling material has generated a lot of interest due to its superior sealing ability and biocompatibility. Although MTA possesses superior sealing ability to traditional endodontic repair filling materials, such as calcium hydroxide, but it has poor handling characteristics. A novel endodontic repair filling materials with s...

INTRODUCTION The aim of the present study was to investigate and compare the apical sealing ability of Resilon/Epiphany-filled root canals with those that were obturated with gutta-percha/AH-Plus endodontic sealer. MATERIALS AND METHODS A total of 60 extracted human single-rooted teeth were selected; 25 teeth for each test group and five for each control group. After conducting conventional e...

The purpose of this study was to evaluate the root-end sealing ability through dye leakage evaluation and the marginal adaptation through scanning electron microscopy (SEM) of some root-end filling materials. Thirty human uniradicular teeth were used. Teeth were divided into three groups: (1) retrofilled with MTA-Angelus, (2) with SuperEBA, and (3) with Vitremer. The root surfaces were isolated...

The aim of this study was to evaluate the sealing ability of materials filled in the orifice after root canal treatment. A total of 100 root canal-treated teeth were divided into six experimental groups: 1, Protect Liner F (PL); 2, Panavia F (PF); 3, DC core-Light cured (DCL); 4, DC core-Chemically cured (DCC); 5, Super-EBA (SE); 6, Ketac (KC). The materials were filled--to a depth of 4 mm--in ...