Consolidated bodies of polycrystalline diamond with grain sizes less than 100 nm, nano-polycrystalline diamond (NPD), has been experimentally produced by direct conversion of graphite at high pressure and high temperature. NPD has superior hardness, toughness and wear resistance to single-crystalline diamonds because of its peculiar nano-textures, and has been successfully used for industrial a...

The zincZeolite Socony Mobil-Five nano-particles (Zn-ZSM-5 NPs) composite was prepared and applied successfully as a new coating material to improve the corrosion resistance of steel. The corrosion type and quality of both pure zinc and our new coating material, Zn-ZSM-5 NPs, were studied using mass loss, impedance and electro-chemical polarization techniques in a sodium chloride solution. Obta...

The nano-threads programming model was proposed to effectively integrate multiprogramming on shared-memory multiprocessors, with the exploitation of fine-grain parallelism from standard applications. A prerequisite for the applicability of the nano-threads programming model is the ability of the runtime environment to manage parallelism at any level of granularity with minimal overheads. In thi...

Nano-scale surface roughness in transparent ITO films was artificially formed by sputtering a mixed Ag and ITO layer and wet etching of segregated Ag nanoparticles from the surface of the ITO film. Effective removal of self-segregated Ag particles from the grain boundaries and surface of the crystalline ITO film led to a change in only the nano-scale surface morphology of ITO film without chang...

The impact of particle size and internal grain boundaries of Beta zeolites was investigated in n-pentane isomerization over bifunctional Pt/Beta catalysts, by comparing the catalytic performance of four assynthesized Pt/Beta samples that possess an identical Pt loading (0.5 wt%), but use four distinct Beta zeolites. Three of them contain polycrystalline zeolites, consisting of nano-sized crysta...

Despite SiGe being one of the most widely studied thermoelectric materials owing to its application in radioisotope thermoelectric generators (RTG), the thermoelectric figure-of merit (ZT) of p-type SiGe is still quite low, resulting in poor device efficiencies. In the present study, we report a substantial enhancement in ZT∼ 1.2 at 900 °C for p-type nanostructured Si80Ge20 alloys by creating s...

The main aim of this research was to find the mechanism for the failure of the CoCrMo porous nano-composite by characterizing microstructural changes and fractured surface after compression test. For this purpose, porous nano-composites were prepared with the addition of bioactive glass nano-powder to Co-base alloy with 22.5% porosity by the combination of space-holder and powder metallurgy tec...

Electrochemical migration (ECM) of sintered nano-Ag could be a serious reliability concern for power devices with high-density packaging. An anti-ECM nano-Ag-SiOx paste was proposed by doping 0.1wt% SiOx nanoparticles rather than previously used expensive noble metals, e.g., palladium. The ECM lifetime the 1.5 to 3 times longer that nano-Ag, due fact protect Ag from oxidation. thermo-mechanical...

Nano-Y2O3 reinforced Ti-47.7Al-7.1Nb-(V, Cr) alloy was fabricated by a powder metallurgy route using spark plasma sintering (SPS), and the influence of nano-Y2O3 contents on microstructure mechanical properties were investigated systematically. The results revealed that ultimate tensile strength elongation 570 ± 28 MPa 1.7 0.6% at 800 °C, 460 23 6.1 0.4% 900 °C with no nano-Y2O3, 662 24 5.5 0.5...

Hydrometallurgical recovery of nano-palladium (Pd) from spent Pd/Al2O3 catalyst has been investigated. The Pd content in the spent catalyst sample was assayed to be 0.42% while the remainder was mainly aluminum oxide. Mixture of HCl and AlCl3 was studied as leaching agent for the sample. The Pd was deposited with formic acid. Different parameters affecting leaching and deposition processes such...