conclusions this study suggested that chlorhexidine had no negative effect on the bond strengths of mta-treated dentin. results there were no statistically significant differences between all the experimental groups. the mode of bond failure was predominantly mixed for distilled water groups and cohesive for chx groups. materials and methods sixty dentin disks with a thickness of 1.5 ± 0.2 mm a...

The purpose of this study was to evaluate the ability of mineral trioxide aggregate (MTA) and amalgam to seal furcal perforations in extracted human molars using an anaerobic bacterial leakage model. Furcal perforations were made in 39 maxillary and mandibular human molars with a high-speed bur. These were randomly divided into two experimental groups of 18, with the remaining three teeth used ...

This study evaluated the biocompatibility of mineral trioxide aggregate (MTA) after direct capping of exposed pulp tissue in dog's teeth. Class I cavities were prepared in 26 teeth from 3 adult dogs. MTA was applied over the exposed pulp in 13 teeth and paste of calcium hydroxide plus distilled water (control) was applied in the remaining 13 teeth. After 90 days, the animals were killed; the ma...

This study was conducted to observe the healing process of intentional lateral root perforation repaired with mineral trioxide aggregate (MTA). Forty-eight root canals of dogs' teeth were instrumented and filled. After partial removal of the filling, an intentional perforation was made with a bur in the lateral area of the root. The perforations were repaired with MTA or Sealapex (control group...

INTRODUCTION This study was carried out to investigate calcific tissue formation against mineral trioxide aggregate (MTA) after pulp capping. MATERIALS AND METHODS The pulps of six teeth from four dogs were exposed and capped with MTA. After extraction each tooth was sectioned into halves. Each half was then further sectioned in the mesiodistal or buccolingual direction. Calcified tissue of t...

Introduction: This study compared the apical sealing ability of a bioceramic based root canal repair filling material (iRoot FS) with mineral trioxide aggregate (MTA). Methods and materials: Forty single-canal teeth were prepared and randomly divided into two experimental groups (n=18) and two control groups (n=2). Teeth in experimental groups were retrofilled with either MTA or iRoot FS. After...

A calcium phosphate cement (CPC) was shown to have the necessary attributes for endodontic materials except adequate basicity needed for antimicrobial properties. To enhance its basicity, tricalcium silicate (Ca3SiO5), a highly alkaline compound, was added to CPC at a mass fraction of 0.25, 0.5 or 0.75. The basicity, acid neutralization and physical properties of the CPC-Ca3SiO5 composites were...

In case of missing permanent successor very often primary teeth may remain retained for longer time beyond their exfoliation schedule. This report demonstrates the functional restorative management a mandibular second molar with successor, treated Mineral Trioxide Aggregate (MTA) as an obturating material. The material seemed to provide biocompatible sealing root canal. After six month follow u...