In this paper, the dynamic responses of cracked beams under different moving forces, including moving load, moving mass, moving oscillator, and four-degrees-of-freedom moving system, are investigated. Structural elements such as beams are designed to withstand the predicted loads, but unfortunately, they are always exposed to unpredictable damage such as cracks. Several factors may cause these ...
Recent experimental and computational work by Link and associates has demonstrated that relatively small (W = 150 mm) single edge notched tension specimens (SE(T)) can be used to obtain crack arrest data high in the ductile-to-brittle transition of ferritic structural steel using dynamic computational techniques if a thermal gradient is utilized to aid in the crack arrest. Testing has been repo...
Catastrophic failure of any brittle structure under dynamic loading consists of dynamic crack initiation, propagation, curving, branching (both micro and macro) and branching instability. However, the failure is much more complex in case of layered materials which has interfaces. In these materials, other than above crack mechanisms the crack can also deflect to propagate along the interface or...
We present an experimental study of the dynamics of rapid tensile fracture in brittle amorphous materials. We first compare the dynamic behavior of “standard” brittle materials (e.g. glass) with the corresponding features observed in “model” materials, polyacrylamide gels, in which the relevant sound speeds can be reduced by 2-3 orders of magnitude. The results of this comparison indicate unive...
The increasing incidence of military aircraft engine failures that can be traced to high-cycle fatigue (HCF) has prompted a reassessment of the design methodologies for HCF-critical components, such as turbine blades and disks. Because of the high-frequency vibratory loading involved, damage-tolerant design methodologies based on a threshold for no crack growth offer a preferred approach. As im...
In this paper we study the crack initiation in a hyper-elastic body governed by a Gri th's type energy. We prove that, during a load process through a time dependent boundary datum of the type t→ tg(x) and in absence of strong singularities (this is the case of homogeneous isotropic materials) the crack initiation is brutal, i.e., a big crack appears after a positive time ti > 0. On the contrar...
In this paper we study the crack initiation in a hyper-elastic body governed by a Griffith’s type energy. We prove that, during a load process through a time dependent boundary datum of the type t → tg(x) and in absence of strong singularities (this is the case of homogeneous isotropic materials) the crack initiation is brutal, i.e., a big crack appears after a positive time ti > 0. On the cont...
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...