For the first time, it has been observed that tin island films used in surface infrared experiments give rise to an electromagnetic enhancement of the infrared absorption spectrum. The surface enhancement of the infrared (SEIR) absorption by tin island films is shown for evaporated nanometric films of 5,14-pentacenedione (Q2) and naphthalic 1,8:4,5-dianhydride (NTCDA). The experiments and spect...

Tin doped In2S3 films were grown by the chemical spray pyrolysis (CSP) method using the pneumatic spray set-up and compressed air as a carrier gas. The spraying solution contained indium chloride (InCl3), thiourea [CS(NH2)2] and (SnCl4) at a molar ratio of S/In = 2.5. The deposition was carried out at 350 °C on glass substrates. The Sn doping level was changed with Sn/In = 0-8 % in solution. Th...

A controllable electrochemical synthesis to convert reduced graphene oxide (rGO) from graphite flakes was introduced and investigated in detail. Electrochemical reduction was used to prepare rGO because of its cost effectiveness, environmental friendliness, and ability to produce rGO thin films in industrial scale. This study aimed to determine the optimum applied potential for the electrochemi...

In this work, the one step electrodeposition process was used to prepare Ag-In-Se thin films. The films were deposited at room temperature from a bath containing 1-3x10 M AgNO3, 6x10 -2 M InCl3 and 3x10 -2 M of H2SeO3. The KSCN at a concentration of 0.681 M was used as complexing agent. The pH value of the solution was 1.4. Applied potentials to SCE were chosen between -0.3 V and -1.1 V. Films ...

We investigate low-temperature transport properties of thin TiN superconducting films in the vicinity of the disorder-driven superconductor-insulator transition. In a zero magnetic field, we find an extremely sharp separation between superconducting and insulating phases, evidencing a direct superconductor-insulator transition without an intermediate metallic phase. At moderate temperatures, in...

Ti0.33Al0.67)1-xSixN (0≤x≤0.29) thin solid films were deposited onto cemented carbide substrates by arc evaporation and analyzed using analytical electron microscopy, X-ray diffraction, nanoindentation, and density functional theory. As-deposited films with x≤0.02 consisted mainly of a metastable c-(Ti,Al)N solid solution for which Si serves as a veritable grain refiner. Additional Si promoted ...

Indium Tin Oxide (ITO) thin films are transparent conducting wide bandgap oxide. In this study investigated optical, structural and morphological properties of sputtered ITO thin films using X-ray diffraction spectroscopy (XRD), Scanning electron microscopy (SEM), Energy Dispersive Spectroscopy (EDX) and optical absorption techniques. These measurements revealed that the oxygen gas percentage p...

Background: Gas sensors are very important in several fields like gas monitoring, safety and environmental applications. In this approach, a new gas sensing concept is investigated which combines the powerful adsorption probability of metal oxide conductive sensors (MOS) with an optical ellipsometric readout. This concept shows promising results to solve the problems of cross sensitivity of the...

Ti-doped ZnO (ZnO/Ti) thin films were grown on indium tin oxide substrates by a facile electrodeposition route. The morphology, crystal structure and resistive switching properties were examined, respectively. The morphology reveals that grains are composed of small crystals. The (002) preferential growth along c-axis of ZnO/Ti could be observed from structural analysis. The XPS study shows the...

TiN films were prepared by the Cathodic arc evaporation deposition method under different negative substrate bias. AFM image analyses show that the growth mode of biased coatings changes from 3D island to lateral when the negative bias potential is increased. Nanohardness of the thin films was measured by nanoindentation, and residual stress was determined using Grazing incidence X ray diffract...