Abstract The paper contains the results of an experimental investigation fatigue crack development under mixed-mode I + II and III in heat-treated 42CrMo4 steel. Tests were performed on compact tension shear specimens rectangular cross-section for III. Mixed-mode tests conducted 30 60° loading angle, while test was 45°. Additionally, presents fracture analysis path development.

An important task in mixed-mode fracture analysis and prediction is the simulation of crack growth under mixed-mode conditions. To complete such a task, one must have (a) a computer code capable of handling the kinematics of general crack growth and determining the stress and deformation states during crack growth, and (b) a fracture criterion that can properly predict the instant and direction...

A new plasticity criterion for mixed mode crack initiation angles under compression is presented, based on the characteristics of the plastic core region surrounding the crack tip with crack surface friction. The shape and size of the plastic core region were thoroughly analyzed under compression and the non-dimensional variable radius of the plastic core region for mixed mode compressive fract...

Delamination is a critical form of failure in composite laminates which is partitioned into a combination of three pure modes namely; opening, shearing and tearing (modes I, II and III respectively). Each fracture mode contributes to the total energy required for delamination growth, due to a combination of the different damage mechanisms that occur under each mode 1-2 . To formulate reliable m...

This paper presents a methodology for conducting a 3-D static fracture analysis with applications to a gas turbine compressor blade. An open crack model is considered in the study and crack-tip driving parameters are estimated by using 3-D singular crack-tip elements in ANSYS . The static fracture analysis is verified with a special purpose fracture code (FRANC3D). Once the crack front is perfe...

The energy release rate (ERR) proposed by Irwin based on a theory by Griffith [1, 2] has been extensively used as a fracture criterion in 2D for brittle domains. Under in-plane mixed mode loading (modes I+II), the direction of crack initiation from cracks and sharp V-notches was determined by the orientation at which the ERR attains its maximum. Using the newly developed asymptotic expansion pr...