in the present study, nanocrystalline ni50al50-xmox (x = 0, 0.5, 1, 2.5, 5) intermetallic compound was produced through mechanical alloying of nickel, aluminum, and molybdenum powders. alni compounds with good and attractive properties such as high melting point, high strength to weight ratio and high corrosion resistance especially at high temperatures have attracted the attention of many rese...

Purpose. Estimation of optimal viscosity a glass lubricant for chromium-nickel steel tube extrusion depending on the deformation resistance, chemical composition metal and temperature, degree rate deformation. Methodology. To determine force conditions extrusion, complex factor resistance was used, which consists in estimating value under basic process parameters plants its refinement deviation...

in this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an al-4.5 wt% cu powder alloy. the wc nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the wc nanoparticles on the mechanical properties of the fabricated composite p...

titanium aluminide and its alloys have been utilized in automotive, aerospace and power industries because of their specific properties such as low density (~ 4 g/cm3), high melting temperature (~ 1460 °c) and excellent high-temperature strength. ti-48al intermetallic compound and its alloys with 1.5, 3 and 5 at.%mn were produced with mechanical alloying of elemental powders for 50 hours. the p...

1 his paper provides a U-J;P,G work for selecting heat exchangers materials especially those used in nuclear power plants. Typical examples of materials selection for heat exchanger tubing of nuclear power plants and condensers are presented. The paper brings out also, the importance of continued intensive R & D in materials in order to enhance the reliability and reduce cost by improving upon ...

This paper reviews the influence of alloying elements Mo, Nb, Ta and Ni on glass formation and corrosion resistance of Cu-based bulk metallic glasses (BMGs). In order to obtain basic knowledge for application to the industry, corrosion resistance of the Cu-Hf-Ti-(Mo, Nb, Ta, Ni) and Cu-Zr-Ag-Al-(Nb) bulk glassy alloy systems in various solutions are reported in this work. Moreover, X-ray photoe...

Surface nanocrystallization using a surface mechanical attrition treatment effectively activates the surface of magnesium alloys due to the increase in grain boundary diffusion channels. As a result, the temperature of subsequent surface alloying treatment of pure Mg and AZ91 alloy can be reduced from 430 degrees C to 380 degrees C. Thus, it is possible to combine the surface alloying process w...