A new and easy-to-make polymer film sensor was prepared by dip-coating technique and this film used as fluorescent chemosensor for the detection of metal ions in aqueous solution. The proposed film sensor exhibited dual emissions at 540 and 582 nm under a single excitation wavelength. The fluorescence behavior of this film sensor toward metal ions has been investigated using these two wavelengt...

Synthesis of structured macroporous TiO2 thin films on quartz substrate (macroTiO2/Q) was performed by a dip-coating method using poly(methyl methacrylate) (PMMA) microspheres as template. Obtained TiO2 thin films kept high transparency and had anatase crystalline structure. SEM observations revealed that the macropores were uniformly formed on the film surface. The size of macropores was quite...

The effects of heat-treatment temperature on LiNbO3 thin films prepared by the polymeric precursor method were investigated. The precursor solution was deposited on Si(111) substrates by dip coating. X-ray diffraction and thermal analyses revealed that the crystallization process occurred at a low temperature (420 °C) and led to films with no preferential orientation. High-temperature treatment...

Sol-gel process was chosen to produce a photocatalytic film to degrade methylene blue. In order to study structural and morphological properties of the coatings, a base sol of TTIP, I-PrOH, and DEA was prepared. Then with addition of 45g/L PEG 2000, 30g/L TiO2 and 15g/L PEG 2000 + 30g/L TiO2, to the base sol, three other sols were produced. The results of this study indica...

Ethanol (C2H6O) sensitivity of zinc oxide (ZnO) thin film has been studied in present work. Semiconductor thin films of zinc oxide (ZnO) were deposited onto alkali-free glass substrates by the sol–gel method and dip-coating technique. The ZnO sol was synthesized by dissolving zinc acetate dehydrate in ethanol, and then adding Tetra ethanol-amine.  The as-coated films were preheated at 150 ºC fo...

Size tunable Cadmium sulphide (CdS) quantum dots have been synthesized through wet chemical co-precipitation method, at three different temperatures 35C, 50C and 65C for varying pH values of 9 and 10.5 respectively. The solution was prepared using Cadmium chloride and thiourea as material precursors, ammonium hydroxide as precipitating agent and mercaptoethanol as surfactant. Thin films of thes...

The aim of this study was to deyelop a noyel hydroxyapatite (HA) coating method on zirconia using glass coating technique. A borosi)icate glass, the mixture of the glass ttnd HA (3e, 50, 70, and 90 mass%), and the 100% HA were coated on two kinds of zirconia discs and fired at 900-950'C. After the final coating, the surface of the sample was etched for 3 min in an acid-mixture of 3% HF and 5%HN...

In this paper, Chitosan-copper nanoparticles were successfully coated onto the Kraft paperusing a dip coating process. First, chitosan-copper nanoparticles solution was prepared byreduction method and the use of ultrasonic radiation. It was employed copper sulphate pentahydrateas precursor salt, NaOH as a reducing agent and Chitosan as capping agent to prepareChitosan-copper nanoparticles solut...