Nanorods of goethite, i.e. alpha-FeOOH, were mixed with BaCO3, dispersed in a polymer solution, and oriented under a 90 kOe magnetic field during polymerization. The orientation arose principally from the interaction of the magnetic field with the anisotropic antiferromagnetism of the goethite particles. The oriented antiferromagnetic particles act as seeds for the topochemical growth of BaFe12...

Magnetic biosensors are an important part of biomedical applications of magnetic materials. As the living tissue is basically a "soft matter." this study addresses the development of ferrogels (FG) with micron sized magnetic particles of magnetite and strontium hexaferrite mimicking the living tissue. The basic composition of the FG comprised the polymeric network of polyacrylamide, synthesized...

The M-type barium hexaferrite substituted with titanium, BaFe12−xTixO19, was synthesized from sodium carbonate flux and the obtained single crystals a maximum degree of substitution up to about x = 0.9 were characterized. XPS measurements carried out for identification side products in particular order assign valence states transition-metal constituents. Due aliovalent exchange iron(III) titani...

The results of studies the features phase composition, crystal and magnetic structure Bi-substituted barium hexaferrite BaFe12-xBixO19 (0.1≤ x≤ 1.2) by methods Mossbauer spectroscopy, X-ray analysis, as well image analysis scanning electron microscopy are presented. Samples hexaferrites - (where x=0.1; 0.3; 0.6; 0.9 were synthesized method solid-phase reactions with double annealing (at T=1100o...

Barium hexaferrite (BaM) films with in-plane c-axis orientation are promising and technically important materials for self-biased magnetic microwave devices. In this work, highly oriented BaM films with different thickness and an in-plane easy axis (c-axis) of magnetization were grown on a-plane single-crystal sapphire substrates by direct current magnetron sputtering. A procedure involving see...

We present experimental results on the hysteresis and relaxation of Fe/Ba hexaferrite composite samples prepared by ball milling starting from precursor Fe and Ba hexaferrite particles. Our results show that, for maximum applied fields of up to 8 kOe, the measured loops show a shift of up to 85 Oe. The compositional dependence of that loop displacement presents two maxima ~at approximately x50....