ESTHETIC REHABILITATION THROUGH CAD/CAM TECHNOLOGY-CASE REPORT (Abstract): With the progress of dental materials and techniques, CAD/CAM system curren tly allows the manufacture of high precision prosthetic restorations. Zirconia is an ideal base for porcelain because the bonding process between the zirconia and the porcelain is stronger than it is with porcelain and metal. This means that the ...

Zirconia doped Hydroxyapatite (HAP) nanocrystals [Ca10(PO4)6-x(ZrO2)x(OH)2]; (0 ≤ x ≤ 1 step 0.2) were synthesized using simple low cost facile method. The crystalline phases were examined by X-ray diffraction (XRD). The crystallinity percentage decreased with increasing zirconia content for the as-synthesized samples. The existence of zirconia as secondary phase on the grain boundaries; as obs...

The thermoluminescence (TL) after excitation by UV or X-rays radiation of doped α-alumina powders is investigated. In the case of zirconia, the alumina-zirconia composites present five of the characteristic peaks of zirconia at –170, –145, –90, 0 and 95°C. After a thermal treatment of mixed oxides, a new peak is observed at –35°C in TL. This peak reveals the presence of stabilized tetragonal zi...

The failure events of Prozyr femoral heads in 2001-2002 have opened a strong, controversial issue on the future of zirconia as a biomaterial. The aim of this paper is to review and analyze the current knowledge on ageing process and on its effect on the long term performance of implants in order to distinguish between scientific facts and speculation. Current state of the art shows the strong v...

OBJECTIVES (1) To synthesize 3mol% yttria-stabilized zirconia (3Y-TZP) powders via coprecipitation route, (2) to obtain zirconia ceramic specimens, analyze surface characteristics, and mechanical properties, and (3) to compare the processed material with three reinforced dental ceramics. METHODS A coprecipitation route was used to synthesize a 3mol% yttria-stabilized zirconia ceramic processe...

PURPOSE The aim of this study was to evaluate the biaxial flexural strength (BFS) of one zirconia-based ceramic used with various veneering ceramics. MATERIALS AND METHODS Zirconia core material (Katana) and five veneering ceramics (Cerabien ZR; CZR, Lava Ceram; LV, Cercon Ceram Kiss; CC, IPS e.max Ceram; EM and VITA VM9; VT) were selected. Using the powder/liquid layering technique, bilayere...

Background and Aim: Application of zirconia ceramics has increased. Since the commonly used surface treatment for porcelain, i.e. acid etching is not efficient for zirconia surfaces, evaluation of other surface treatment methods for zirconia is important. The aim of this study was to compare the shear bond strength (SBS) of metal brackets to zirconia treated with different powers of Er:YAG lase...

INTRODUCTION Since it is not possible to form an adequate micromechanical bond between resin cement and zirconia ceramics using common surface treatment techniques, laser pretreatment has been suggested for zirconia ceramic surfaces. The aim of this study was to evaluate the effect of Carbon Dioxide (CO2) Laser treatment on shear bond strength (SBS) of resin cement to zirconia ceramic. METHOD...

OBJECTIVES It is difficult to achieve adhesion between resin cement and zirconia ceramics using routine surface preparation methods. The aim of this study was to evaluate the effects of CO2 and Er:YAG laser treatment on the bond strength of resin cement to zirconia ceramics. MATERIALS AND METHODS In this in-vitro study 45 zirconia disks (6 mm in diameter and 2 mm in thickness) were assigned t...

PURPOSE The purpose of this in vitro research project was to evaluate and compare the wear behavior of human tooth enamel opposing monolithic zirconia and other different ceramic restorative materials and also to observe the tetragonal to monoclinic phase transformation in zirconia-based ceramics that may occur while simulating wear occurring at room temperature in a wet environment. MATERIAL...