Non-corrosive, carbon-based materials are usually used as anodes in microbial fuel cells (MFCs). In some cases, however, metals have been used that can corrode (e.g. copper) or that are corrosion resistant (e.g. stainless steel, SS). Corrosion could increase current through galvanic (abiotic) current production or by increasing exposed surface area, or decrease current due to generation of toxi...
In this article, the failure of a heat exchanger during its operation in the marine environment has been analyzed. This heat exchanger was used for cooling the oil in a marine diesel engine. Based on the existing failure history, damages in engine components were observed after 89 hours of engine working due to the leakage of the sea water to the oil. For the objective of the failure analysis, ...
Low carbon steel has been considered a suitable material for component of the multi-barrier system employed on the geological disposal of high-level radioactive waste (HLW). A non negligible amount of dihydrogen (H2) is expected to be produced over the years within the geological repository due to the anoxic corrosion of metallic materials and also to the water radiolysis. The influence of the ...
Two coastal seawaters (Key West, FL, USA and the Persian Gulf, Bahrain, representing oligotrophic and eutrophic environments, respectively) were used to evaluate potential biodegradation and corrosion problems during exposure to alternative and conventional fuels. Uncoated carbon steel was exposed at the fuel/seawater interface and polarization resistance was monitored. Under typical marine sto...
Corrosion is constantly a major problem of the world economy in the field of metal products, metal processing and other areas that utilise metals. Previously used compounds utilizing hexavalent chromium were amongst the most effective materials for corrosion protection but regulations have been recently introduced that forbid their use. Consequently, there is a huge drive by engineers, technolo...
Corrosion can be affected by flow differently depending on the mechanism governing the corrosion process. Two major cases can be distinguished: the effect of flow on corrosion when no surface films are present and the effect of flow on corrosion in the presence of surface films (precipitates, inhibitors, etc.). In the absence of films, the primary effect of flow on corrosion is through mass tra...
Corrosion of steel reinforcement is one of the main durability problems facing reinforced concrete infrastructures worldwide. This paper will summarize the results of a multi-phase experimental program undertaken at the University of Waterloo to investigate the viability of using externally bonded fiber reinforced polymer (FRP) laminates to rehabilitate corrosion-damaged reinforced concrete bea...
As bioabsorbable materials, magnesium alloys are expected to be totally degraded in the body and their biocorrosion products not deleterious to the surrounding tissues. It's critical that the alloying elements are carefully selected in consideration of their cytotoxicity and hemocompatibility. In the present study, nine alloying elements Al, Ag, In, Mn, Si, Sn, Y, Zn and Zr were added into magn...
key words: Lead corrosion, Raman spectroscopy, oxide reduction, organic acids, electrochemistry Even though kept in cultural institutions, artefacts can be subjected to accelerated deterioration due to high concentration of pollutants in closed spaces. Potentially harmful conditions have been evaluated by electrochemical reduction of corrosion products formed on metallic coupons which have been...