Nearly monodisperse cobalt ferrite (CoFe2O4) nanoparticles without any size-selection process have been prepared through an alluring method in an oleylamine/ ethanol/water system. Well-defined nanospheres with an average size of 5.5 nm have been synthesized using metal chloride as the law materials and oleic amine as the capping agent, through a general liquid–solid-solution (LSS) process. Magn...

In this work we have examined the influence of the pH on the structural and magnetic properties of cobalt ferrite (CoFe2O4) nanoparticles obtained by a combination of the co-precipitation and hydrothermal methods. The crystal structures and the particle sizes of the prepared powders were analyzed by the X-ray diffraction and transmission electron microscopy, while the magnetic properties of the...

BACKGROUND/AIM Metal-ceramic bond strength and alloys' elastic modulus clearly determine the potential of alloy application, because the ceramic integrity during mastication depends on these two characteristics. The aim of this study was to evaluate metal-ceramic bond strenght and elastic modulus of cobalt-chromium alloys in making porcelain-fused-to-metal restorations, regarding the applicatio...

Nearly monodisperse cobalt ferrite (CoFe2O4) nanoparticles without any size-selection process have been prepared through an alluring method in an oleylamine/ethanol/water system. Well-defined nanospheres with an average size of 5.5 nm have been synthesized using metal chloride as the law materials and oleic amine as the capping agent, through a general liquid-solid-solution (LSS) process. Magne...

Cobalt ferrite nanoparticles were synthesized with coprecipitation or with the hydrothermal method. Stable water suspensions were prepared from the as-synthesized nanoparticles, with the addition of citric acid as a surfactant, and then used for the preparation of deposits under an applied magnetic field. The morphology of the cobalt ferrite nanoparticles was investigated with a transmission el...

The temperature dependence of the magnetic properties of titanium modified cobalt ferrite is presented. The change of maximum magnetization obtained at H ≈ 2.4 MA/m between any two temperatures increases systematically with composition, which is desirable for applications in devices. Variation in magnetocrystalline anisotropy and coercivity were different from previous studies on cation substit...

nt matter & 2013 0.1016/j.nanoen.2 thor. Tel.: (65)-67 [email protected] (P Abstract In this work, we present the formation of porous NiCo oxide nanowires from single crystal nickel cobalt bimetallic carbonate hydroxide nanowires (NiCo cNW) for supercapacitor applications. High aspect ratio NiCo cNWs are found to evolve from highly crystalline nickel cobalt layered double hydroxides through a dode...