Natural and modified zeolites (0.5-1.0 mm) from the Tasajera deposit in Cuba were used to enhance the anaerobic digestion process of synthetic substrates. Natural zeolites were modified by ionic exchange and by adsorption with nickel, cobalt and magnesium. The experiments were carried out by using an inoculum from a full-scale anaerobic reactor treating winery wastewater. Modified natural zeoli...

The effects of anodizing condition and post treatment on the growth of nickel nanowires, were investigated. A two-step anodizing process was applied in phosphoric and oxalic acid solution. Nickel electrochemical plating was applied to fill Anodic Aluminum Oxide (AAO) pores. For pore filling enhancement, AAO surfaces were treated by silver predeposition. After electroplating, aluminum and oxide ...

Methyl orange is one dye resulted from the textile industry. The aim of this study is to test theadsorption capacity of nickel oxide nanoparticles for removing the methyl orange from aqueoussolution. The parameters studied were the effect of temperature, contact time and initial pH ofsolution. Results indicate that the removal efficiency of nickel oxide nanoparticles increases withincreasing co...

Nickel oxide (NiO) nano-size powder is synthesized using nickel (II) acetate tetrahydrate, sodium lauryl sulfate (SLS) and ammonia as precursors. Applied surfactant is anionic surfactant. The sample was characterized by FT-IR, X-ray diffraction (XRD), scanning electron microscopy (SEM). The results obtained confirm the presence of nickel oxide nano-powders produced during chemical precipitation...

Nickel oxide (NiO) nano-size powder is synthesized using nickel (II) acetate tetrahydrate, sodium lauryl sulfate (SLS) and ammonia as precursors. Applied surfactant is anionic surfactant. The sample was characterized by FT-IR, X-ray diffraction (XRD), scanning electron microscopy (SEM). The results obtained confirm the presence of nickel oxide nano-powders produced during chemical precipitation...

he inherent lightness and good strength-to-weight ratio of T magnesium has focused attention on increasing applications in aerospace and allied fields. Its density is two thirds that of aluminum-a conventional structure material for aerospace. Magnesium has one drawback: It is prone to atmospheric corrosion. Further, because of its high chemical affinity for aqueous solutions, it is categorized...

Iron–nickel spinel oxide NiFe2O4 nanoparticles have been prepared by the combination of chemical precipitation and subsequent mechanical milling. For comparison, their analogue obtained by thermal synthesis is also studied. Phase composition and structural properties of iron–nickel oxides are investigated by X-ray diffraction and Mössbauer spectroscopy. Their catalytic behavior in methanol deco...

The potential of near infrared spectroscopy (NIR) with remote reflectance fiber-optic probes for determining the mineral composition of propolis was evaluated. This technology allows direct measurements without prior sample treatment. Ninety one samples of propolis were collected in Chile (Bio-Bio region) and Spain (Castilla-León and Galicia regions). The minerals measured were aluminum, calciu...

In the current paper,Nanostructured Nickel oxide (NiO) were synthesized by co-precipitation method using Nickel(II) Chloride Hexahydrate (NiCl2.6H2O) and sodium hydroxide (NaOH) as starting material. Structural, optical and magnetic properties of nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Atomic force microscope (AFM), UV–Vis absorption; Fo...

Generation and entrance of toxic materials to aqueous environment causes many problems human health. In the current study, removal efficiency Cd (II) Ni(II) from solution was investigated by carbonaceous magnesium oxide. Three types C-MgO adsorbents were synthesized via pyrolysis prepared complex Mg(acac)2 at three temperatures. Fabricated characterized XRD, SEM, BET. XRD results revealed that ...