Investigations were carried out to study the effects of heat treatment on the mechanical properties of rolled medium carbon steel. The steel was heated to the austenizing temperature of 830C and water quenched; It was reheated to the ferrite – austenite two phase region at a temperature of 745C below the effective Ac3 point. The steel was then rapidly quenched in water and tempered at 480C to p...

To clarify the mechanism of acicular ferrite formation in low carbon submerged arc weld metals of a Ti-B system with different aluminum contents, the lattice misfit between inclusion and acicular ferrite was investigated. The inclusions were directly sliced into thin foils by a focused ion beam device and crystallographic analyses were performed using a transmission electron microscope. These i...

17-4PH stainless steel is a martensitic precipitation hardening stainless steel that provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties, good toughness in both base metal and welds, and short time, low-temperature heat treatments that minimize warpage and scaling. This valuable alloy is widely used in the aerospace, nuclear, chemical, pet...

Steel bracing members are widely used in steel structures to reduce lateral displacement and dissipate energy during earthquake motions. Concentric steel bracing provide an excellent approach for strengthening and stiffening steel buildings. Using these braces the designer can hardly adjust the stiffness together with ductility as needed because of buckling of braces in compression. In this stu...

The present research was designed to evaluate an ultrasonic technique for measuring the drawability of low carbon steel sheets nondestructively. This technique, which uses electro magnetic acoustic transducers (EMAT's) is embodied in a fully automatic ultrasonic device called Ultra-Form, which was developed at Iowa State University (by the Center For Nondestructive Evaluation) in 1990. EMAT tra...

The effect of tempering on the mechanical properties, structure, and dispersion secondary phase particles is studied in 0.4%C-2%Si-1%Cr-1%Mo-VNb steel. This steel austenitized at 900 °C with subsequent water quenching exhibits a yield stress 1445 MPa lath martensite structure MX ~40 nm located matrix boundary M6C carbides ~210 nm. Tempering temperature interval 200–400 provides 1625 due to prec...