Aim. To compare and evaluate the microleakage in class V lesions restored with composite resin with and without liner and injectable nanohybrid composite resin. Materials and Methodology. 60 class V cavities were prepared in 30 freshly extracted teeth. After etching and application of bonding agents these cavities were divided into three groups: Group A (n = 20)-restored with composite resin, G...

The relationships between the transmission coefficient and the cure depth were evaluated on eight commercially available light-activated resin composites. The determination of transmission coefficient was carried out by the use of a radiometer for various shades of the resin composites. The transmission coefficient, ranging from 0.042 to 0.263, wasdependent upon the shade of the resin. There wa...

OBJECTIVE This study was undertaken to determine the effect of temperature on the microhardness and viscosity of 4 resin composite materials. METHODS To investigate microhardness, samples of each of the 4 composite materials, prepared by standard insertion of resin into prefabricated moulds, were divided into 2 groups (n = 10 per group). On the first group, the resin composite materials were ...

Background and Aim: The aim of this study was to evaluate the micro-shear bond strength of an indirect composite resin to three different types of cores. Materials and Methods: In this in-vitro study, 14 blocks (5×5×2 mm) were designed and milled by computer from cobalt-chromium (Co-Cr) alloy, zirconia, and polyether ether ketone (PEEK). Each sample was treated according to the manufacturer’s ...

OBJECTIVES To determine the retentive strength and failure mode of undercut composite post, glass fiber post and polyethylene fiber post luted with flowable composite resin and resin-cement. MATERIALS AND METHODS Coronal parts of 120 primary canine teeth were sectioned and specimens were treated endodontically. The teeth were randomly divided into 6 groups (n = 20). Prepared root canals recei...

BACKGROUND Although composite restorations are really valuable for esthetic zones, they have shown less longevity rather than amalgam restorations. Since it may be related to the method used for curing the composite, postcuring could increase the degree of conversion and result in more long-lasting composite restorations. This study was planned to evaluate the effect of two different postcuring...

This study evaluated the effects of the light curing methods and resin composite composition on composite polymerization contraction behavior and resin composite adaptation to the cavity wall using μCT-3D visualization analysis and dye penetration test. Cylindrical cavities were restored using Clearfil tri-S Bond ND Quick adhesive and filled with Clearfil AP-X or Clearfil Photo Bright composite...