The compressive creep and recovery of foam earplugs was studied at various applied stresses leading to different fi nal creep strains. Deformation was determined from digital videos of the earplugs via image processing software. Creep could not be modeled by a single exponential in time; creep approximated a power law in time. Nonlinear viscoelasticity was observed: creep compliance depends on ...

In this study, a real and significant industrial problem in a steam power plant was investigated. Reheater tubes in boilers are under the creep and the fireside corrosion mechanism that cause some of them to fail. Since the estimation of probability of failure (PoF) and remaining life (RL) is expensive and time consuming in the deterministic methods, in this work they were evaluated using struc...

Using nano-technology materials in the asphalt pavement industry is new compared with Portland cement concrete. The main objective of this study is to investigate the effects of nano-silica modification on some properties of a penetration grade asphalt cement and a typical asphalt concrete. 60/70 penetration grade bitumen was modified with different percentages of nano-silica (i.e. 1, 3 and 5%,...

All three burning plasma experiments discussed at Snowmass during the summer of 2002, use preloaded structures to resist some component of the operating loads. For the resistive pulsed reactors, it is the preloads which introduce the most noticeable creep responses because these loads are applied for much longer than the operating loads. If the preloads are maintained during shut-down and maint...

In order to characterize the creep behaviors of 2219 aluminum alloy at different temperatures and stress levels, a RWS-50 Electronic Creep Testing Machine (Zhuhai SUST Electrical Equipment Company, Zhuhai, China) was used for creep experiment at temperatures of 353~458 k and experimental stresses of 130~170 MPa. It was discovered that this alloy displayed classical creep curve characteristics i...

Strain-controlled continuous fatigue and creep–fatigue tests were carried out at 700 °C 800 on Inconel 625 alloy. The effects of strain rate tensile-hold time cyclic stress response life investigated. Then, the microstructural analysis fractographic fatigue-fractured specimens performed by scanning electron microscopy transmission microscopy. responses during high-temperature creep–fatigue–oxid...