The problem of fatigue-crack-growth in a rotating disc at different crack orientation angles is studied by using an automated numerical technique, which calculates the stress intensity factors on the crack front through the three-dimensional finite element method. Paris law is used to develop the fatigue shape of initially semi-elliptical surface crack. Because of needs for the higher mesh dens...

We give a precise mathematical formulation of a variational model for the irreversible quasi-static evolution of a brittle fracture proposed by G.A. Francfort and J.-J. Marigo, and based on Griffith’s theory of crack growth. In the two-dimensional case we prove an existence result for the quasi-static evolution and show that the total energy is an absolutely continuous function of time, althoug...

Modelling quasi-static crack growth with interface elements is a widely accepted technique [1-2]. Interface elements are inserted into the finite element mesh along possible crack paths. The interface elements are characterised by a traction-displacement curve. When a specific maximum stress is reached, the interface element undergoes a softening process until the critical fracture energy has b...

An important task in mixed-mode fracture analysis and prediction is the simulation of crack growth under mixed-mode conditions. To complete such a task, one must have (a) a computer code capable of handling the kinematics of general crack growth and determining the stress and deformation states during crack growth, and (b) a fracture criterion that can properly predict the instant and direction...

Finite element method (FEM) is one of the most famous methods which has many applications in varies studies such as the study of crack propagation in engineering structures. However, unless extremely fine meshes are employed, problem arises in accurately modelling the singular stress field in the singular element area around the crack tip. In the present study, the crack growth simulation has b...

The corrosion fatigue crack growth characteristics of small (>35pm) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500X) crack length measurements in laboratory air and 1% NaCl environments. To quantify the “small crack effect” in the corrosive environment, the corrosion fatigue crac...

THE SELF STRESS field and self energy are estimated for a planar 3D dislocation loop emanating from a halfplane crack tip. While the problem is of greatest interest for analysis of shear loops nucleating from the crack tip in the concentrated stress field there due to applied loadings, it is addressed here in the interest of tractability for 3D prismatic loops lying in the same plane as the cra...

Precracked and notched specimens were used to investigate the fracture mechanism of a bainite steel at low temperature. The critical fracture event was studied using metallographic sectioning method. The results showed that the critical cleavage event was different in the precracked and the notched specimens. At -196C, all specimens fractured at lower-shelf region without any ductile crack grow...

Fatigue crack growth behavior of AZ61 magnesium alloy was investigated in low humidity (55% relative humidity) and 3.5% NaCl spray environments under various stress ratios. Fatigue crack growth rates became higher with increasing load ratio for both environments. However, the results of fatigue crack growth test under 3.5% NaCl spray environment showed lower fatigue crack propagation rate compa...

This paper studies the application of an inverse methodology for problem solving in fracture mechanics using the finite element analysis. The method was applied to both detection of subsurface cracks and the study of propagating cracks. The procedure for detection of subsurface cracks uses a first order optimization analysis coupled with a penalty function to solve for the unknown geometric par...