STATEMENT OF THE PROBLEM Polymerization shrinkage stress in composite restorations may lead to microleakage. Clinical methods such as using low-shrinkage composites have been suggested to overcome this problem; however, there are controversies about their efficiency in decreasing the microleakage. PURPOSE This in vitro study was conducted to compare the microleakage of two low-shrinkage resin...

Glass ionomer cement, besides being used as restorative material, can also be used as pit and fissure sealant. The use of glass ionomer cement as pit and fissure sealant has added benefit by its fluoride-releasing property that results in increased resistance of the fissures to demineralize. The capacity of a sealant to prevent microleakage into the fissure is important, since microleakage may ...

Introduction: Disinfection of the cavity preparation after caries excavation can lead to the elimination of bacterial remnants that can be responsible for recurrent caries, postoperative sensitivity, and failure of the restoration. The purpose of this study was to evaluate the effects of two disinfectants on microleakage of composite restorations in primary teeth. Metho...

Rhodamine B, a fluorescent substance, was used as a tracer to investigate in vitro early microleakage from around amalgam restorations in machinable mica glass-ceramic after thermal stress. Five types of amalgam, i.e., low-copper spherical, low-copper lathe-cut, high-copper admixture, high-copper lathe-cut, and high-copper spherical, were examined in the present study. The results indicated tha...

The purpose of this study was to compare (a) forces generated during lateral compaction and (b) apical microleakage for nickel-titanium (NiTi) and stainless steel (SS) finger spreaders. Twenty-eight extracted human teeth were instrumented using a standardized rotary instrumentation technique. NiTi and SS #30 spreaders were used to obturate molar roots while the forces generated during obturatio...

AIM Our study aimed to analyze the microleakage of silorane-based composite in comparison to two homologous methacrylate-based composites. MATERIALS AND METHODS Standardized class I cavities (4 × 2.5 × 3 mm) were prepared on extracted human premolars and randomly assigned into three groups (N = 15) as follows: Group A, Filtek P90 (silorane) with its dedicated adhesive system (P90 system adhes...

The aim of this investigation was to test the hypothesis that there is no difference in microleakage between composite-enamel and composite-wire interfaces, when different composites are used. Forty-five freshly extracted human mandibular incisors separated into three groups were used in the study. Multi-stranded 0.0215 inch diameter wire was bonded to enamel using two conventional (Transbond X...

AIM AND OBJECTIVES Fissure caries is most common in children due to deep pit and fissures. Pit and fissure areas on the occlusal surface of the teeth make them susceptible to dental caries, which need to be prevented or restored. Fissures sealant reduces the risk of occlusal caries. The present study was done to evaluate microleakage and shear bond strength of various fissure sealants. MATERI...