Depending on the starting equilibrium temperature, the application of a magnetic field on a sample of Ni–Mn–Sn produces sample heating or cooling during adiabatic experiments. The competition between endothermal and exothermal effects is observed close to the martensite-to-austenite magnetostructural phase transition. A model assuming the coexistence of two phases and a field dependence of thei...

The microstructure of 8 mm diameter wire produced by the severe deformation of 316L austenitic stainless steel has been examined using TEM and X-ray diffraction. The deformation imparted amounts to a true strain of 6.3. Data from previous studies on strain induced transformation of this steel have been combined with new results to show that true strains .2 are required in order to observe mecha...

Susceptibility of three lean-alloyed ferritic-austenitic stainless steels to hydrogen-induced delayed cracking was examined, concentrating on internal hydrogen contained in the materials after production operations. The aim was to study the role of strain-induced austenite to martensite transformation in the delayed cracking susceptibility. According to the conducted deep drawing tests and cons...

The work reports an experimental observation on crystal rotation in a duplex (austenite + ferrite) steel induced by the electropulsing treatment at ambient temperature, while the temperature rising due to ohmic heating in the treatment was negligible. The results demonstrate that electric current pulses are able to dissolve the initial material's texture that has been formed in prior thermomech...

in the present study, the effect of grain size on the austenite stability was studied by nanoindentationtests in a 304l stainless steel. thermomechanical processing based on cold rolling and annealing wasused to produce two different types of austenite: ultrafine grained (ufg) austenite with the averagegrain size of 0.65 μm and coarse grained (cg) austenite with the average grain size of 12 μm....

The microstructure and mechanical properties of Zr48Cu48 - x Al4M x (M ≡ Fe or Co, x = 0, 0.5, 1 at.%) metallic glass (MG) composites are highly dependent on the amount of Fe or Co added as microalloying elements in the parent Zr48Cu48Al4 material. Addition of Fe and Co promotes the transformation from austenite to martensite during the course of nanoindentation or compression experiments, resu...

INTRODUCTION To improve the fracture resistance of nickel-titanium (NiTi) files, manufacturers have introduced new alloys and developed new manufacturing processes for the fabrication of NiTi files. This study aimed to examine the phase transformation behavior and microstructure of NiTi instruments from a novel controlled memory NiTi wire (CM wire). METHODS Instruments of EndoSequence (ES), P...

There are two well-known phenomena associated with the bainite reaction, both of which have been exploited here to enhance the mechanical behaviour of steel. Firstly, the bainite plate size decreases as the transformation temperature is reduced. Secondly, it is bad to have large regions of untransformed austenite in the microstructure; this is because they can transform, under the influence of ...

The effects of increasing nickel from 3 to 7 and 9 wt. % were investigated in high strength steel weld metals with 2 wt. % manganese. It was found that nickel additions were positive for strength but negative for impact toughness. Significant segregation of nickel and manganese to interdendritic regions was observed with the two higher nickel contents. In these weld metals a mainly martensitic ...