Energy dissipation on collisions of grain aggregates is investigated taking into account effects by sintering. It is shown that sintering significantly reduces the energy dissipation efficiency because contacts between adjacent grains become strong by sintering.

UNLABELLED Most flash sintering experimental set-ups use dog bone-shaped specimen and DC current, which results in heterogeneously distributed densification and grain growth throughout the sample. This is the reason why only the sample's core characteristics after flash are taken into account. On the other hand, some recent procedures suggest the use of cylindrical pellets, which have some adva...

PURPOSE The purpose of this study was to compare the optical properties of pre-colored dental monolithic zirconia ceramics of various thicknesses sintered in a microwave and those in a conventional furnace. MATERIALS AND METHODS A2-shade of pre-colored monolithic zirconia ceramic specimens (22.0 mm × 22.0 mm) in 3 thickness groups of 0.5, 1.0, and 1.5 mm were divided into 2 subgroups accordin...

To investigate the effect of sintering temperature and sintering time on arsenic volatility and arsenic leaching in the sinter, we carried out experimental works and studied the structural changes of mineral phases and microstructure observation of the sinter at different sintering temperatures. Raw materials were shaped under the pressure of 10 MPa and sintered at 1000~1350°C for 45 min with a...

Sintering of supported metal catalysts is of primary interest in heterogeneous catalysis. The presence of reactant gases, especially oxidants, often accelerates the sintering of supported metal catalysts. Our in situ studies using scanning tunneling microscopy (STM) compare the sintering of Au particles supported on TiO2(110) in the presence of CO, O2, or mixtures of the two gases. The results ...

Nanohydroxyapatite-carbon nanotube composite coatings were deposited via electrophoretic deposition (EPD). AISI 316L stainless steel and ethanol were used as substrate and dispersing medium, respectively. 5%wt carbon nanotube (CNT) was used as reinforcing phase. Uniform and macrocrack-free coatings were obtained both for hydroxyapatite (HA) and HA-5%wt CNT coatings. Scanning electron micros...